Effect of preparation route on the degradation behavior and ion releasability of siloxane-poly(lactic acid)-vaterite hybrid nonwoven fabrics for guided bone regeneration
スポンサーリンク
概要
- 論文の詳細を見る
Two types of nonwoven fabric, consisting of siloxane-doped vaterite (SiV) and poly(lactic acid) (PLA), for guided bone regeneration (GBR) were prepared by an electrospinning. One of the fabrics, SiV-PLA(M), was derived from PLA mixed with the solution of SiV dispersed in chloroform. Another one, SiV-PLA(K), was derived from a composite prepared by kneading SiV and PLA while heating at 200°C. The SiV-PLA(K) fabric shows higher degradability in dilute NaOH aq. than the SiV-PLA(M) fabric. To improve the cellular compatibility of the fabric, the fibers were coated with hydroxyapatite (HA) by soaking in simulated body fluid. The HA-coated SiV-PLA(K) fabric showed the release of silicate ions; the amount was reduced by 1/5 to 1/8 compared with that of the HA-coated SiV-PLA(M) fabric, and the excessive release was controlled. The preparation route of kneading at 200°C led to formation of a fabric with degradation behavior and ion releasability effective for bone regeneration.
論文 | ランダム
- 青年の自己実現をめざす学校経営の転換(課題研究I 青年期(高校段階)における自己実現のための課題)
- 教授・学習過における教育資料・情報について
- 教育経営における情報システムの研究
- 高校生の生活意識と生徒指導のすすめかた : とくに性、生きがい、特別教育活動をめぐって(第6部会〔高校教育〕)
- 新人運動選手の左室心筋重量と有酸素性作業能力の関係