高窒素オーステナイトステンレス鋼の組織と機械的性質に及ぼす時効の影響
スポンサーリンク
概要
- 論文の詳細を見る
The effect of aging on microstructures and mechanical properties of 1%N-23%Cr-4%Ni-2%Mo austenitic stainless steel aged at 600∼800°C for up to 1000 h were investigated with electron microscope, analysis of extracted residues, ferrite scope, and mechanical tests such as hardness, tensile, and Charpy impact. Chromium nitrides precipitated on grain boundary at the aging temperature below 650°C, while lamellar precipitates, which were composed of plate like Cr2N and martensite, were formed above 700°C. σ phase precipitated at 700°C for 1000 h and above 750°C for longer than 100 h. Martensite was also observed around σ phase, and the total amount of martensite was 40-50% after aging at 700-800°C for 1000 h. Age hardening was observed above 700°C and hardness, which increased with aging time and temperature, reached about Hv 500 after aging at 800°C for 1000 h. Increase in tensile strength by aging was higher than that in proof strength, because of pronounced increase in work hardening rate by aging. Strengthening by aging depended mainly on the amount of lamellar precipitates and additionally on σ phase and its surrounding martensite at higher temperature. Tensile ductility and impact toughness were decreased by aging due to lamellar precipitates and σ phase.
論文 | ランダム
- 幻の「赤城根鉱山」に藍銅鉱と孔雀石を探す
- メディアとしての動画投稿サイト : その文化性と事業性(ワークショップ6,2008年度秋季研究発表会 ワークショップ報告)
- パーソナルムービーの公共性 : 個人記録映像の上映会とアーカイブ化の実践より(第31期第4回研究会(マルチメディア研究部会企画),研究会の記録(2007年12月〜2008年5月))
- コミュニティの非営利放送運営における新公益法人制度の検討(地方のコミュニティメディアにおける非営利放送に関する研究,共同研究)
- 地域のコミュニケーション・インフラの持続可能性 : 非営利コミュニティ放送の運営調査から(荒牧和子教授退職記念号)