鋳片表層組織制御による圧延鋼片の表面疵防止
スポンサーリンク
概要
- 論文の詳細を見る
This study was carried out in order to make clear the crack generation mechanism of case-hardening steels.It was suggested from the average oxide particle radius around surface cracks of the rolled billets that most of the surface cracks should be generated at the bloom rolling process.From the point of view of surface crack generation at the rolling process, austenite grain sizes just before rolling were pointed out. In general, in order to prevent surface cracks at the rolling process, bainite or ferite/bainite structure before reheating is suitable for fine grain structure just before rolling. In order to get these structures, the cooling rate of the bloom surface should be higher than 2.0K/s under the cooling start temperature of 1023-1173K. It was proved that refining austenite grain in the bloom surface just before rolling was effective to decrease the crack generation.
論文 | ランダム
- 東方旅行記における二つの観察潮流とそのトポス--フランス大使ダラモン一行におけるキリスト教古代文化と異文化の取り扱い
- 7.心内血栓の超音波診断と経過観察 : 左房,及び左室内血栓各1例について(第620回千葉医学会例会・第2回千葉大学第3内科懇話会)
- トルコ古典文学における都市と詩人--都市トポスの誕生と16世紀イスタンブル
- トルコ古典文学における酌人--17世紀オスマン朝「酌人の書」についての一考察
- 書評と紹介 ハルン・トラサ『セヒー,ラティーフィー,アーシュク・チェレビーの詩人列伝に見る16世紀の文学研究と文学批評』 Harun Tolasa, Sehi, Latifi, Asik Celebi Tezkirelerine gore 16. Yuzyilda Edebiyat Arastirma ve Elestirisi