高Crフェライト系耐熱鋼溶接継手の組織評価
スポンサーリンク
概要
- 論文の詳細を見る
Microstructures of KA-SCMV28, KA-STPA29 and KA-SUS410J3 weld joints were investigated mainly by electron backscatter diffraction pattern (EBSP) in order to clarify the differences of fine grained HAZ formation mechanism among these steels. The welded specimens were heat treated at 740-760°C for several hours as the post weld heat treatment (PWHT). In the base metal of KA-SCMV28 and KA-STPA29, most of the observed boundaries were block and packet boundaries and the ratio of the boundaries with rotation angle of 60° was high. In the fine grained HAZ region of these steels, boundaries with rotation angles of 22 to 46°, which were different from K-S relationship, were detected and the ratio of block boundaries with rotation angle of 60° decreased. In order to investigate the formation mechanism of fine grains, as-welded specimen of KA-SCMV28 without PWHT was observed. Boundaries (22-46°) which were different from K-S relationship have already formed in the as-welded condition but the ratio of these boundaries was lower than in the specimen after PWHT. It was considered that fine grains were formed by the transformation of α’ to γ to α’ or α’ to α during welding cycle. On the other hand, in KA-SUS410J3 most of boundaries were block and packet boundaries and distinct fine grain region was not observed. In addition, distribution of the rotation angle was not much different between the base metal and HAZ region.
著者
関連論文
- 種々の荷重モードによりひずみを付与した低炭素ステンレス鋼の粒界近傍における方位差分布評価
- 高Crフェライト系耐熱鋼溶接継手のクリープ劣化
- 高温排気ガス対応ターボチャージャ向けタービンインペラ材料の各種特性 (新技術・新製品特集号)
- 高Crフェライト系耐熱鋼溶接継手の組織評価
- Ni基超合金U720LIの組織安定性におよぼす応力負荷の影響
- S0306-1-4 EBSD法によるステンレス鋼の歪み解析に及ぼす諸因子の影響([S0306-1]損傷の結晶解析的評価)
- 650℃で引張ひずみを付与したオーステナイト鋼のEBSDひずみ解析に及ぼす結晶粒径の影響
- 704 火SUS304J1HTBの変形における粒内ひずみならびに粒界での方位差分布の温度依存性(エネルギー・発電プラント機器,一般セッション)
- 418 火SUS304J1HTBのクリープに及ぼす予ひずみの影響(クリープII,高温材料の変形・破壊・損傷評価と実機への適用,オーガナイスドセッション2)
- 602 オーステナイト鋼のEBSD歪み解析に及ぼす粒径の影響(クリープ・クリープ疲労と損傷,高温材料の損傷・寿命評価の展開,オーガナイスドセッション2)
- 515 EBSDによる高Crフェライト系耐熱鋼の塑性ひずみ評価(ミクロ組織,高温強度に影響する諸因子,オーガナイスドセッション2)
- 650℃で引張ひずみを付与したオーステナイト鋼のEBSDひずみ解析に及ぼす結晶粒径の影響
- Ni基鍛造合金U 720 LIの部分溶体化処理によるγ'析出形態と機械的特性の制御
- オーステナイト系ステンレス鋼ならびにニッケル基合金における結晶方位回転の塑性ひずみ依存性
- オーステナイト系ステンレス鋼ならびにニッケル基合金における結晶方位回転の塑性ひずみ依存性