フルオロアルキル鎖を有するエチレン−マレイミド共重合体薄膜の凝集構造と表面特性
スポンサーリンク
概要
- 論文の詳細を見る
We investigated the aggregation structure and surface properties of ethylene-maleimide copolymer thin films as a function of fraction of fluoride side group by means of small angle X-ray scattering (SAXS), grazing incidence SAXS (GISAXS), DSC, and contact angle measurements. The maleimide copolymers were synthesized through the imidization of poly(ethylene-alt-maleic anhydride) with stearylamine and fluoroalkyl amine. The thin films were obtained by spin-coating on silicon wafers and annealed at appropriate temperatures. The copolymer having fluoroalkyl side chains (SFχ) form ordered structure when fluorine side chain content is more than 40%. The copolymer SFχ attached with stearyl and fluoroalkyl side chains formed the layered structure no less than 40 mol% of fluoroalkyl side group. In the thin film, the layer was found to be aligned parallel to the substrate as revealed by GISAXS and AFM. The surface free energy of the SFχ was revealed to decrease steeply around 40mol% of fluoroalkyl side group. The surface segregation of the fluorine groups linked to the ordered structure formation.
著者
関連論文
- フルオロアルキル鎖を有するエチレン−マレイミド共重合体薄膜の凝集構造と表面特性
- Polybutadiene-block-Poly (ε-caprolactone) ブロック共重合体が形成する結晶-非晶交互ラメラ繰り返し構造から Gyroid 構造への相転移挙動
- ポリメチルメタクリレート固体表面のガラス転移温度
- ジブロック共重合体が形成するミクロ相分離構造中のマトリックスブロックの自由末端セグメントの分子運動特性
- Polybutadiene-block-Poly (ε-caprolactone) ジブロック共重合体の相挙動 : 比較的低分子量で秩序-無秩序転移を示す系の相挙動について
- 選択スピンラベル法による高分子鎖の局所分子運動解析 : ブロック共重合体のミクロ相分離構造と局所分子運動
- 同時測定 小角X線散乱と複数プローブの同時測定による結晶性高分子材料の階層的高次構造の形成過程の研究 (小角散乱特集)
- 高速紡糸ポリエチレンテレフタレート繊維のシンクロトロンX線散乱法による精密構造解析
- 小角・広角X線/偏光解消小角光散乱同時測定による結晶性高分子の構造解析
- ESRスピンラベル法による高分子ダイナミックスの研究
- 小角・広角X線散乱/Hv光散乱同時測定による直鎖状低密度ポリエチレン/ゴムブレンド中での結晶化挙動の解析
- 電子スピン共鳴のマイクロ波出力飽和現象を利用した高分子のガラス転移温度評価
- On-Line Wide-Angle X-Ray Scattering Measurements During High-Speed Melt-Spinning of Poly(Ethylene Terephthalate) Fiber