Enhancement of piezoelectric constant d33 in BaTiO3 ceramics due to nano-domain structure

スポンサーリンク

概要

• 論文の詳細を見る

• BaTiO3 ceramics with different domain sizes were prepared by spark plasma sintering (SPS) and normal sintering (NS) using hydrothermally synthesized 100 nm and 500 nm powders. It was found that their piezoelectric constant d33 shows great dependence on the size of ferroelectric domains. A high d33 up to 416 pC/N was obtained in the SPSed ceramics derived from 100 nm powders, whose domain width was identified <50 nm by transmission electron microscopy (TEM). However, the d33 values are 216 and 193 pC/N, respectively for the BaTiO3 ceramics prepared by SPS using 500 nm powders and by NS using 100 nm powders, whose microscale domains can be observed by optical microscopy.

著者

• Li Jing-feng

  State Key Laboratory Of New Ceramics And Fine Processing Department Of Materials Science And Enginee

• Shen Zong-Yang

  State Key Laboratory of New Ceramics and Fine Processing, Department of Materials Science and Engine

• Li Jing-Feng

  State Key Laboratory of New Ceramics and Fine Processing, Department of Materials Science and Engineering, Tsinghua University

• SHEN Zong-Yang

  State Key Laboratory of New Ceramics and Fine Processing, Department of Materials Science and Engineering, Tsinghua University

関連論文

• Enhancement of piezoelectric constant d33 in BaTiO3 ceramics due to nano-domain structure
• Photostrictive Characteristics of Fine-Grained PLZT Ceramics Derived from Mechanically Alloyed Powder
• Preparation of (100)- and (111)-Textured Pb(Zr,Ti)O3 Piezoelectric Films and Direct Measurement of Their Piezoelectric Constants
• High Normalized Strain Obtained in Li-Modified (K,Na)NbO_3 Lead-Free Piezoceramics

スポンサーリンク