Low-Temperature Synthesis of Porous Praseodymium Oxysulfate Oxygen Storage Materials by Using a CTA Template

スポンサーリンク

概要

• 論文の詳細を見る

• Porous praseodymium oxysulfate, Pr2O2SO4, with a large oxygen storage capacity was prepared from precipitates, which were formed by adding (NH4)2SO4 to a mixed aqueous solution of Pr(NO3)3 and cationic surfactant, CTA (cetyltrimethyl ammonium ion). Heating the precipitate, Pr-SO4-CTA, yielded directly the single phase of Pr2O2SO4 at a low temperature of 300°C, compared to ≥800°C required for the decomposition of Pr2(SO4)3 (Pr-SO4), and compared to ≥500°C required for the mesophase of Pr and dodecyl sulfate (Pr-DS) in our previous study.1) The effect of preparation route on microstructure and oxygen release/storage property of Pr2O2SO4 was studied by using XRD, TG, SEM, N2 adsorption and catalytic reaction. In contrast to the macropores (≥30 nm in size, 8 m2g-1) of Pr-SO4 and mesopores (≤10 nm, 28 m2 g-1) of Pr-DS, Pr-SO4-CTA showed a wide pore size distribution in the range 2-40 nm and a larger surface area of 37 m2 g-1. The porous structure is very effective in increasing the rate of oxygen release as well as storage. The anaerobic CO oxidation of 1 mass% Pd-loaded Pr2O2SO4 was evaluated in CO/O2 cycled feed stream reactions. It was found that the catalyst prepared from Pr-SO4-CTA achieved the highest catalytic activity due to the high porosity and specific surface area.

• 公益社団法人 日本セラミックス協会の論文

著者

• Zhang Dong-jie

  Department Of Nano Science And Technology Graduate School Of Science And Technology Kumamoto Univers

• Machida Masato

  Department Of Applied Chemistry And Biochemistry Graduate School Of Science And Technology Kumamoto University

• Ikeue Keita

  Department Of Applied Chemistry And Biochemistry Graduate School Of Science And Technology Kumamoto University

• Zhang Dong-Jie

  Department of Nano Science and Technology, Graduate School of Science and Technology, Kumamoto University

• ETO Masakazu

  Department of Nano Science and Technology, Graduate School of Science and Technology, Kumamoto University

• IKEUE Keita

  Deparment of Applied Chemistry and Biochemistry, Graduate School of Science and Technology, Kumamoto University

関連論文

• Synthesis of ZrP2O7 by hydrothermal reaction and post-calcination
• Promotion of Methane Steam Reforming Using Ruthenium-Dispersed Microporous Alumina Membrane Reactor
• Liquid Phase Formation of Spinel Surface Layers on Hexaaluminate Microcrystals
• Gas Permeation through Microporous Alumina Membranes Containing Highly Disperesed Metal Particles
• Catalytic soot oxidation by Ag/BaCeO3 having tolerance to SO2 poisoning
• Enhanced Photocatalytic Water Splitting of Hydrous LiCa_2Ta_3O_ Prepared by Hydrothermal Treatment
• Electrocatalytic Reduction of Nitrate Using Cu-Pd and Cu-Pt Cathodes/H^+-Conducting Solid Polymer Electrolyte Membrane Assemblies
• Crystallization of Calcium Phosphate Templated by α-Amino Acids Depending on Their Composition, Chain Length, and Enantiomerism
• Intercalation of Dendritic Polyamines by α- and γ-Zirconium Phosphates
• Photocatalytic Reduction of CO_2 with H_2O on Titanium Oxides Prepared within the FSM-16 Mesoporous Zeolite
• Synthesis of large surface area MnO_x-CeO_2 using CTA and its catalytic activity for soot combustion( Innovative Ceramic Materials and Technologies for Global Environmental Protection)
• Thermostable Rh Catalysts Supported on Metal Phosphates : Effect of Aging on Catalytic Activity for NO-CO-C_3H_6-O_2 Reactions
• Effect of heat treatment on local structure and photocatalytic water splitting activity of Ni-loaded LiCa2Ta3O10
• Structure and CO Oxidation Activity of Pt/CeO_2 Catalysts Prepared Using Arc-Plasma
• Structure and Catalytic Properties of Pd/10Al_2O_3・2B_2O_3・Effect of Preparation Routes and Additives
• Low-Temperature Synthesis of Porous Praseodymium Oxysulfate Oxygen Storage Materials by Using a CTA Template
• Nanometric Colloidal Sols of CeO_2-ZrO_2 Solid Solution as Catalyst Modifiers. I. Preparatioon and Structure

もっと見る 閉じる

スポンサーリンク