Processing of porous silicon carbide with toughened strut microstructure
スポンサーリンク
概要
- 論文の詳細を見る
Porous SiC ceramics were fabricated by the carbothermal reduction of polysiloxane-derived SiOC containing hollow microspheres followed by sintering. The effect of the Al2O3–Y2O3–CaO (AYC) content on the microstructure and flexural strength of the porous SiC ceramics were investigated. The growth of large platelet α-SiC grains increased with increasing additive content due to enhanced grain growth and the β → α phase transformation of SiC. In situ toughened microstructures consisting of large platelet grains and fine equiaxed grains were obtained when 10 or 20 wt% AYC was added. The porosity generally decreased with increasing the additive content, whereas the flexural strength increased. The typical flexural strength of the porous SiC ceramics sintered with 10 wt% AYC was 61 MPa at a porosity of 44%.
著者
-
Eom Jung-Hye
Department of Materials Science and Engineering, the University of Seoul
-
Kim Young-wook
Department Of Materials Science And Engineering The University Of Seoul
-
NARISAWA Masaki
Department of Materials Science, Graduate School of Engineering, Osaka Prefecture University
-
Eom Jung-hye
Department Of Materials Science And Engineering The University Of Seoul
関連論文
- Processing of porous silicon carbide with toughened strut microstructure
- ポリシロキサンと高分子マイクロビーズの押し出し成形体からの多孔質シリコンオキシカーバイドセラミックスのプロセシング
- Effect of aluminum source on flexural strength of mullite-bonded porous silicon carbide ceramics
- Effect of submicron silicon carbide powder addition on the processing and strength of reaction-sintered mullite-silicon carbide composites
- Effect of filler addition on porosity and strength of polysiloxane-derived porous silicon carbide ceramics
- 高分子液体の泡立てと圧縮金型成形による多孔質シリコンオキシカーバイドセラミックスの作製
- Analysis of Silicon Carbide Particle Formation Process from Carbon Black-Phenolic Resin-Ethyl Silicate Hybrid Precursors
- Silicon carbide particle formation from carbon black : polymethylsilsesquioxane mixtures with melt pressing
- 空孔量を制御した多孔性コーディエライトセラミックスのプロセシング
- Reaction Mechanism of the Pyrolysis of Polycarvosilane and Polycarbosilazane as Ceramic Precursors
- SB-05-5(123) Temperature-Atmosphere Dependence of Creep Behavior of Advanced SiC-Based Fibers(Ceramic, Polymer and Composites)
- Synthesis of SiO2–TiO2 fibers with photocatalytic activity by TiCl4 vapor curing on melt-spun silicone resin fiber
- Effect of additive composition on porosity and flexural strength of porous self-bonded SiC ceramics
- Suppression of free Si formation during liquid phase sintering of polysiloxane-derived, porous silicon carbide ceramics
- 炭化ケイ素ナノ粒子の焼結性
- Effect of template size on microstructure and strength of porous silicon carbide ceramics(Glass and Ceramic Materials for Photonics)
- SiC-TiC複合材の高靭化機構
- Effect of additives on compressive strength and thermal conductivity of vermiculite-silica composites with layered structure
- Effect of template size on microstructure and strength of porous silicon carbide ceramics
- Positive Correlation Between the Dysregulation of Transforming Growth Factor-β1 and Aneurysmal Pathological Changes in Patients With Marfan Syndrome
- Positive Correlation Between the Dysregulation of Transforming Growth Factor-β_1 and Aneurysmal Pathological Changes in Patients With Marfan Syndrome