Fe-Sm急冷薄帯のメカニカルグライディングによる相変化
スポンサーリンク
概要
- 論文の詳細を見る
The Fe-Sm binary alloy ribbons were prepared by melt spinning technique. The prepared alloys with Sm 8.7 and 12.7 at% were mainly composed of TbCu7 metastable phase. In addition, α-Fe in Sm 8.7 at% and Fe2Sm in Sm 12.7 at% alloy were also observed. In contrast to them, the alloy with Sm 27.5 at% has an amorphous phase. After mechanical grinding (MG) for 72 ks under N2 atmosphere, the alloys with Sm 8.7 and 12.7 at% showed the phase transition to the metastable state coexisting of α-Fe and Fe-Sm amorphous phase. On the other hand, the alloy with Sm 27.5 at% showed the crystallization after the MG from amorphous phase to Fe-Sm-O phase. The MGed alloys with Sm 8.7 and 12.7 at% were heated up to 1027 K. After the heating, the alloy with Sm 8.7 at% was composed of α-Fe, FeN, Fe-Sm-N and Fe3O4. On the other hand, the metastable phase was still sustained in the alloy with Sm 12.7 at%.
論文 | ランダム
- 差分次数の変化に伴うIARモデリングの最適フィルタ次数の変動
- 環境音の音源認識システムについて
- 環境音の音源認識の前処理について
- 短時間測定における非定常時系列のモデル化について
- 動的モデルによる非定常時系列の同定について