In Situ Observation of Creep and Fatigue Failure Behavior for Plasma-Sprayed Thermal Barrier Coating Systems
スポンサーリンク
概要
- 論文の詳細を見る
In order to investigate crack initiation sites and the crack propagation behavior in connection with the microstructure of thermal barrier coating (TBC) systems under creep and fatigue loadings, the failure behavior was observed in situ for plasma-sprayed TBC systems by optical microscopy, as a first step for elucidating the thermo-mechanical failure mechanism. Two types of TBC systems with differing top-coat (TC) microstructures were prepared by changing the processing conditions. The mechanical failure behavior of TBC system was found to depend strongly on the loading conditions. Under static creep loading, many segmentation cracks in the TC widened with increasing creep strain in the substrate. However, the propagation of these cracks into the bond-coat (BC) and alloy substrate was prevented due to the stress relief induced by plastic flow in the BC layer at elevated temperatures. As a result, the TBC system exhibited typical creep rupture behavior with nucleation and coalescence of microcracks in the alloy substrate interior regardless of the TC microstructure. Under dynamic fatigue loading, on the other hand, many fatigue cracks initiated not only from the tips of segmentation cracks in the TC layer but also from the TC/BC interface. Furthermore, it was found that the fatigue cracks propagated into the BC and alloy substrate even at elevated temperatures above the ductile-brittle transition temperature of the BC; the fatigue failure behavior under dynamic fatigue loading was dependent on the TC microstructure and the properties of the TC/BC interface.
論文 | ランダム
- 最近の中国における五四運動研究について(太平天国史学術討論会・報告特集)
- 四国の旅 : 山本憲のことなど (研究調査紀行)
- 京都における小学校創立時の教材をめぐって : 『万国公法』のことなど : 平成十七年五月十一日(水) (月例研究会(二〇〇〇五年度)報告要旨)
- Synthesis of oxidized fatty acid derivatives via an iodolactonization reaction
- 言葉と心を育てる国語科の授業 (小特集 言葉と心を育む国語科の指導)