EBSD Observation of Micro Crack Morphologies after Thermal Exposure in Thermal Barrier Coatings

スポンサーリンク

概要

• 論文の詳細を見る

• Micro-cracking process in TBCs(Thermal Barrier Coatings) due to thermal exposure was investigated using SEM(Scanning Electron Microscope) and EBSD(Electron BackScatter Diffraction) observation. Splat particle morphologies in TBCs were clearly visualized by IPF (Inverse Pole Figure) mapping. The splat structure of top coat was consisted with large granular particle region and cluster of small columnar particle region. Cracks were observed along the interfaces of large granular particle region and the cluster of small columnar particle region, along the interfaces among large granular particles and across the cluster of small columnar particles transgranularly perpendicular to columnar crystal growth direction. The onset time of extensive macro crack formation was corresponding to the Cr oxide growth at TGO(Thermally Grown Oxide) to some extent. Thus EBSD observation can be used as a powerful tool for crystallographic observation of TBC, associated with SEM and optical microscope observation.

著者

• FUJIYAMA Kazunari

  Department of Mechanical Engineering, Faculty of Science and Technology, Meijo University

• KIMACHI Hirohisa

  Department of Mechanical Engineering, Nagoya University

• KATO Yukihiro

  Graduate School of Mechanical Engineering, Meijo University

• NAKASEKO Hikaru

  Graduate School of Mechanical Engineering, Meijo University

• KIMACHI Hirohisa

  Department of Mechanical Engineering, Meijo University

関連論文

• Collaborative Research on Adhesion Strength of Thermal Barrier Coatings in JSMS
• EBSD Observation of Micro Crack Morphologies after Thermal Exposure in Thermal Barrier Coatings
• Single Crystal Elastic Constants of β-Silicon Nitride Determined by X-Ray Powder Diffraction
• Lattice Strain and Domain Switching Induced in Tetragonal PZT by Poling and Mechanical Loading
• X-Ray Stress Measurement of TiN Thin Film with Fiber Texture under External Loading
• Prediction of Propagation Path of Matrix Cracks in FRP under Remote Mode I Loading(Composite 3)
• Transition from Small to Large Interlaminar Cracks in Fiber-Reinforced Laminated Composites
• Damage Assessment of Heat Resistant Steels through Electron BackScatter Diffraction Strain Analysis under Creep and Creep-Fatigue Conditions

スポンサーリンク