Effect of Shear Speed on the Ball Shear Strength of Sn–3Ag–0.5Cu Solder Ball Joints
スポンサーリンク
概要
- 論文の詳細を見る
The effect of shear speed on the ball shear strength of Sn–3wt%Ag–0.5wt%Cu solder ball joints has been investigated. The effect of electrode type on shear strength under various aging conditions was also studied. A linear relationship was obtained between the logarithm of shear speed and the ball shear load in the joints with Cu electrodes, regardless of aging conditions. Fracture occurs in the solder at lower shear speeds (below 10–3 m/s) in joints both with Cu and with electroless Ni–P/Au plated electrodes. The fracture mode changes from a solder fracture to an intermetallic compounds (IMC) fracture at higher shear speeds (above 0.5 m/s), regardless of electrode type. This means a ductile-to-brittle transition exists in the shear speed range from 10–3 m/s to 0.5 m/s. In the case of the joint with the Ni–P/Au electrode, shear strength decreases at higher shear speeds (above 0.5 m/s) due to the ductile-to-brittle transition.
論文 | ランダム
- 眼科学用語ノート : 5. 略語(頭字語 acronym)の使用現況
- 超伝導薄膜のハイパワーマイクロ波特性の測定法(マイクロ波超電導/一般)
- 眼科学用語ノート : 4. 眼圧や屈折度の数量表記
- 眼科学用語ノート : 3. c-spelling と k-spelling : disc/disk, phaco-/phako-
- 超伝導薄膜のハイパワーマイクロ波特性の測定法(マイクロ波超電導/一般)