Surface Oxidation of Low Carbon Steel Strip during Batch Annealing
スポンサーリンク
概要
- 論文の詳細を見る
Selective oxidation of low carbon strip steels industrially batch annealed in 4% hydrogen 96% nitrogen atmosphere was studied using scanning electron microscopy (SEM) and transmission electron microscopy (TEM). It was found that the selective oxidation was not uniform across the width of the steel strip. The non-uniformity of the selective oxidation across the strip width produced the localised formation of (MnFe)O and MnCr2O4 particles along the ferrite grain boundaries, mainly in the vicinity of the strip edge region. The distribution of the MnCr2O4 particle sizes within this region can explain the generation of a defect on the final tinplate product, which manifests as a localised band of low reflectivity after tinplating of batch annealed strip, ‘edge defect’ that can be produced on batch annealed tinplate. The propensity for nitrogen absorption was also found to vary significantly across the strip width and was limited in the region where selective oxidation occurred. This non-uniformity in selective oxidation and nitrogen absorption is probably due to the changes in the dewpoint or oxygen potential of the annealing gas across the width of the strip.
論文 | ランダム
- パルプ黒液を含むバイオブリケットのガス化反応速度解析
- Ca(OH)_2を含む石炭ブリケットの燃焼における脱フッ素特性(論文賞,平成17年度 日本エネルギー学会)
- 22-42 脱硫プロセスからの廃棄物による中国東北部アルカリ土壌改良メカニズムの検討(22.環境保全,日本土壌肥料学会 2005年度大会講演要旨集)
- Ca(OH)_2を含む石炭ブリケットの燃焼における脱フッ素特性
- 中国炭中フッ素の形態と燃焼時のフッ素の挙動