Tempering Process and Precipitation Behavior of 8%Cr–2%WTa Steel
スポンサーリンク
概要
- 論文の詳細を見る
In order to clarify the stability of precipitates in 8%Cr–2%W–0.09%Ta steel at high temperatures, tempering and precipitation behavior of the steel has been examined precisely. Tempering was performed mainly at 740°C for 0.5–1 000 h. Hardness peak was found in a tempering curve at 650–740°C for 3.75–8 h. Discontinuous changes in X-ray diffraction intensity of the matrix, apparent lattice strain and apparent crystalline particle size, which were estimated from integral breadth, the amount of extracted residue, and the Cr and Ta content in the residue were observed at 740°C for 2–12 h tempering. These discontinuous changes correspond to the rotation of preferred orientation or the generation of subgrains accompanying the dissolution and the subsequent re-precipitation of M23C6 and TaC. The re-precipitation of fine M23C6 particles is responsible for the hardness peak. Three kinds of TaC with different chemical composition and different size are found. The amount and the size of the coarse and medium TaC particles are affected by the discontinuous changes in microstructure. Fine particles of TaC grow very slowly, which is caused by the continuous dissolution of TaC due to the annihilation of precipitation site, dislocations, and re-precipitation on dislocations. Particle sizes of TaC and M23C6 estimated using X-ray diffraction peak coincide with those observed in transmission electron microscopy.
論文 | ランダム
- 国際協力の取り組み 北東アジアのシームレス物流環境の構築と韓国の対応 (特集 2009北東アジア経済発展国際会議(NICE)イン新潟) -- (分科会D 北東アジア・シームレス物流)
- 学生指導に使用できる熱伝導率の視覚的測定法 (特集 計測(その2))
- 婦人用靴下着用による足の形態へ及ぼす影響について
- 学校教育における肌着着用に関する実態調査--通学時ならびに体育授業時における実態
- サ-モグラフィによる日傘の防暑効果に関する衛生学的研究