The Role of New Ferrite on Retained Austenite Stabilization in Al-TRIP Steels
スポンサーリンク
概要
- 論文の詳細を見る
Microstructure and mechanical properties of two high Al, low-Si TRIP steels with different Cr and Mo contents were studied using continuous galvanizing line (CGL) laboratory simulation. Combined use of specific etching methods, optical and electron microscopy observations and EBSD characterization led to verify the epitaxial growth of ferrite during cooling at a moderate rate from the intercritical annealing to the isothermal holding temperature. The amounts of “new” ferrite formed during cooling and retained austenite obtained after processing are much higher in the steel with lower content of hardenability-promoting elements. Measured tensile properties and mechanical behavior of the steel strongly depend on the amount of new ferrite and retained austenite. It is found that the formation of new epitaxial ferrite from intercritical austenite can effectively contribute to the chemical and particle size stabilization of untransformed austenite as well as to obtain the desired TRIP effect under processing conditions highly compatible with industrial practice, i.e. cooling rates near 15°C/s and isothermal holding times at 460°C shorter than 60 s.
論文 | ランダム
- エゾボラNeptunea polycostataの繁殖生態,特に成熟サイズ,生殖周期と性比について
- P1-18 抗透明帯自己抗体が卵巣障害の原因となりうるか?(高得点生殖医学1,高得点演題プログラム,第59回日本産科婦人科学会学術講演会)
- 関西医科大学における精路再建術 : 精路閉塞原因の最近の動向もふくめて
- MP-590 膀胱がん細胞における放射線照射後の小核形成、多核化、核変形の原因について(一般演題ポスター,第94回日本泌尿器科学会総会)
- マウスautoimmune regulator (aire) タンパク質の局在に関する組織学的解析