Electrical Resistance Change Measurement with Elevated Temperature due to Joule Heating for the Detection of Delamination in Graphite/Epoxy Composites
スポンサーリンク
概要
- 論文の詳細を見る
Delamination cracks in a graphite/epoxy composite change the thermal expansion properties in the damaged regions. We detect this change by measuring the electrical resistance in the affected areas while heating. The proposed damage detection method is effective even when a damaged electrode is used, in contrast to the traditional method, which requires highly reliable electrodes to prevent an increase of the inherent electrical resistance. The proposed damage detection method is thus feasible for a variety of environments that might cause the degradation of the electrode. Heating of the composite is performed by Joule heating of the graphite fibers rather than general heating using an outside heat source. Graphite fibers, due to their high electrical conductivity, are used not only as the damage sensor but also as the heat source. The influences of delamination and electrode defects on a heated cross-ply beam are examined by simulation. The electrical resistance change after Joule heating is also experimentally measured. As a result, we proved that delamination detection is possible even with a damaged electrode.
論文 | ランダム
- 水稲の減数分裂期における幼穂の位置とかんがい水深について
- 米のたんぱく含量に関する研究 : 第6報 葉面散布された尿素窒素の穂への移行と米粒たんぱく質含有率
- 減数分裂期の気温が登熟歩合に及ぼす影響について : 昭和55年水稲冷害の実例
- 種子の貯蔵養分の消長と幼植物の生育
- 44 水稲の冷害に関する研究 : 第4報 冷害被害軽減例 : N追肥と被害程度