The Tribological Characteristics of Ni-Cr Cast Alloy at 1000 Degree C in Air
スポンサーリンク
概要
- 論文の詳細を見る
Ni-Cr alloy sliding tests in the atmosphere at 1000 °C which is higher than the temperatures used in the conventional research were carried out and observed the process in which glazed oxide layer is formed on the wear track. By the analysis of the element distribution on the cross-section of the glazed oxide layer formed on the wear track after the friction had been reduced, we have clarified that the glazed oxide layer formation process is the same as the process found by the conventional research. Furthermore, the discharge of wear particle necessary for the formation of glazed oxide is further promoted at 1000 °C and therefore glazed oxide begins to form on the comparatively early stage, thereby showing low friction and low wear.
著者
-
Ohmae Nobuo
Department Of Mechanical Engineering Faculty Of Engineering Kobe University
-
Yokoyama Fumihiko
Machine Elements Dept. Research Laboratory, IHI Corporation
-
Yamasaki Takahiro
Fundamental Research and Engineering Dept., IHI Inspection & Instrumentation Co., Ltd
-
Yoshihisa Junichi
Machine Elements Dept. Research Laboratory, IHI Corporation
関連論文
- Formation of Thin Oxide Films on Room-Temperature Silicon (100) by Exposure to a Neutral Beam of Hyperthermal Atomic and Molecular Oxygen
- Oxidation Properties of Hydrogen-Terminated SI (001) Surfaces Following Use of a Hyperthermal Broad Atomic Oxygen Beam at Low Temperatures : Instrumentation, Measurement, and Fabrication Technology
- The Tribological Characteristics of Ni-Cr Cast Alloy at 1000 Degree C in Air
- Effect of Low-Energy Ion Bombardment upon Field-Stimulated Exoelectron Emission from Tungsten Surfaces
- Surface Reaction of a Low-Flux Atomic Oxygen Beam with a Spin-Coated Polymide Film : Synergetic Effect of Atomic Oxygen and Ultraviolet Exposures
- Surface Reaction of a Low Flux Atomic Oxygen Beam with a Spin-Coated Polyimide Film : Translational Energy Dependence on the Reaction Efficiency
- Effects of External Stresses on the Low Temperature Thermal Oxidation of Silicon
- Surface Characterization of Carbon Fibers Exposed to 5 eV Energetic Atomic Oxygen Beam Studied by Wetting Force Measurements
- High growth rate of vertically aligned carbon nanotubes using a plasma shield in microwave plasma-enhanced chemical vapor deposition
- High friction of a vertically aligned carbon-nanotube film in microtribology
- Study on Near Dry Machining of Aluminum Alloys(Advanced Manufacturing Technology [I])
- Synthesis and mechanical properties of carbon nanotube/diamond-like carbon composite films
- Frictional Properties of Carbon Nanotube Films with a Load Range from Micronewton to Millinewton Using mm Size Balls