概要

• 論文の詳細を見る

• Adhesion between two clean surfaces was investigated using a surface-activated bonding method in an ultrahigh vacuum (UHV) at room temperature. Adhesion was observed in all combinations of SUS440C/Ti-6Al-4V, INCONEL718/Ti-6Al-4V, A7075/SUS440C, SUS304/Al and INCONEL718/SUS440C. To understand the basic problems of UHV bonding, the influence of the surface roughness on bonding strength and interface structure has been studied. The surface roughness at the nanometer scale strongly influenced the bonding strength. In the case of SUS304 and Al, surfaces with less than l nm (RMS) had a high bonding strength of over 80 MPa. The interface does not have a thick reaction layer, only an amorphous layer on the order of several nanometers. Separation of the SUS304/Al interface by heat treatment has been also studied. A specimen heated at 823 K for 2 hr in a vacuum separated spontaneously without any external mechanical force. Separation occurred at the interface between the Al and the layer of the reaction products. This separation occurred only if the specimen was heated in a vacuum or argon atmosphere. The specimen did not separate when it was heated in air, nitrogen or oxygen atmospheres. The separated SUS304 could be re-bonded to Al at room temperature.

• 社団法人 日本航空宇宙学会の論文

著者

• IMAGAWA Kichiro

  Japan Aerospace Exploration Agency

• SUGA Tadatomo

  University of Tokyo, RCAST

• HOSODA Naoe

  National Institute for Materials Science

• OBARA Shingo

  Japan Aerospace Exploration Agency

• Suga Tadatomo

  University Of Tokyo Department Of Precision Engineering School Of Engineering

• SUGA Tadatomo

  University of Tokyo

関連論文

• Butt Welding Joint of Aluminum Alloy by Space GHTA Welding Process in Vacuum
• Effect of Long Time Orbit Exposure Test on Solid Lubricative Coating
• SB-8-32 Evaluation and Analysis of the First-Retrieved Unit of the Space Environment Exposure Device : SM/MPAC&SEED(Space Experiment)(SB-8. Results of Various Satellite Missions)
• Welding Experiments of Aluminum Alloy by Space GHTA Welding at ISS Orbital Pressure
• Development of Space DL Welding Process for Construction and Repair of Space Structures in Space
• InGaAsP Laser on GaAs Fabricated by the Surface Activated Wafer Direct Bonding Method at Room Temperature
• Water Direct Bonding at Room Temperature by Means of the Surface Activated Bonding
• Low-Temperature Au-to-Au Bonding for LiNbO_3/Si Structure Achieved in Ambient Air(Micro/Nano Fabrication,Microoptomechatronics)
• UHV-Bonding and Reversible Interconnection
• Finite element analysis of nanometer-scale contact for low temperature bonding

スポンサーリンク