Crystallization Behaviors of Mold Fluxes Containing Li2O Using Single Hot Thermocouple Technique
スポンサーリンク
概要
- 論文の詳細を見る
Minor addition of Li2O (<2 mass%) can significantly alter the melting temperature and viscosity of a mold flux. However, the crystallization tendency of mold fluxes containing Li2O more than 2 mass% hasnt been understood. In this paper, single hot thermocouple technique, X-ray diffraction, and Back Scattered Electron (BSE) were employed to investigate the crystallization behavior concerned with CCT and TTT diagrams of mold fluxes containing high content of Li2O.The critical cooling rate and crystallization rate of samples were increased with the addition of Li2O, whether there is Na2O or not. But the incubation time was reduced obviously with Li2O more than 6 mass% in mold fluxes. The critical cooling rate and incubation time of NL1.5 sample (Na2O=8 mass%, Li2O=1.5 mass%) were close to those of L7 sample (Na2O=0 mass%, Li2O=7 mass%). Moreover, there is no difference in the crystal phase of the two samples, and the crystal phases precipitated at high temperature and low temperature were respectively Ca2(SiO4) and Ca4Si2O7F2. Li-cuspidine was promoted to precipitate when the basicity of the sample was increased. The small, dense grains of cuspidine were observed in NL1.5 sample, and the thickness of slag film was 0.4 mm more than that of L7 sample. The heat flux of NL1.5 sample measured was 10% less than that of L7 sample, as expected. Therefore, high content of Li2O can be substituted by the combination of Na2O and minor of Li2O, as is the composition in the commercial mold fluxes.
論文 | ランダム
- 妊娠高血圧症候群とその管理 (特集 妊娠高血圧症候群)
- 妊婦の高血圧 (女性外来診療マニュアル) -- (症状・症候から診断・治療へ--産科編)
- Slow-fast Form of Atrioventricular Nodal Reentrant Tachycardia with Unusual Retrograde Activation in the Right Atrium : Possible Conduction Disturbance across the Tendon of Todaro Related to the Genesis of Positive Component of Biphasic Retrograde P Wave
- ハムスター血漿α-1-antiproteinaseのcDNA塩基配列の決定およびmRNAの発現状態の検討
- FEAL-NXのソフトウェア実装