High Temperature Characterization of CO2 Treated Fluxed Pellets Developed for Basic Oxygen Steel Making
スポンサーリンク
概要
- 論文の詳細を見る
Presently, use of lump lime in BOF is often associated with operational problem due to its high melting point (~2700°C), poor dissolution property, fines generation, hygroscopic nature. Lime in combination with iron oxide is expected to quickly dissolve into steel making bath to produce low melting point oxidizing slag and to make the refining process faster. In current study, the suitability of a fluxed pellet containing 20–40% lime and waste iron oxides, developed through a novel binderless palletizing process where the strength was developed by CO2 treatment at room temperature has been tested for use in BOF. The pellets were characterized at low temperature as well as high temperature. The softening point of pellet was determined by TG-DTA and fusion study was carried out in muffle furnace. The results indicate early melting in BOF operating temperature. The pellet exhibited reasonable thermal shock resistance property, considered essential for the intended use in BOF. Deterioration of (Cold Crushing Strength) CCS on high temperature treatment is not likely to restrict its use in steel making furnace.
論文 | ランダム
- 冠拡張剤、抗動脈硬化剤併用投与による薬剤結果について : 第69回日本循環器学会関東甲信越地方会
- 心電図、脈波速度検査所見と冠硬化の対比および疫学的調査結果について : 第69回日本循環器学会関東甲信越地方会
- 斜波中における航洋プッシャーバージの連結部に働く波浪荷重について
- 13.トリオソルブM-125の基礎的検討(◇第9回中部部会)
- 12.コンテソルブー125の基礎的検討(◇第9回中部部会)