Adsorption properties of high-silica zeolites for high-temperature chemical heat pumps.
スポンサーリンク
概要
- 論文の詳細を見る
To evaluate their usability as adsorbents in chemical heat pumps for high-temperature use (over 373 K), an accelerated aging test by steam was performed for various zeolites and the adsorption equilibria of selected zeolites were measured. from the high-temperature steaming test it was found that high-silica zeolites like <I>Na-mordenite</I>, <I>USY</I> (ultrastable Y) and <I>HY</I> had higher thermal stability than conventional A- or X-type zeolite. Further, measurements of isotherms of <I>Na-mordenite</I> and <I>USY</I> showed that they maintained adsorption capacity even at 473 K. Acquired isosters of each zeolite and water were approximated as straight lines in the range from room temperature to 473 K. On their charts, heat transformer (chemical heat pump) cycles that work at high temperatures could be generated. High-silica zeolites like <I>Na-mordenite</I> or <I>USY</I> are therefore expected to be usable as adsorbents of water for repeating chemical heat pump operations at high temperature, though their total adsorption capacities are smaller than those of A- or X-type zeolites.
著者
-
SUZUKI Kunio
National Institute of Materials and Chemical Research, Tsukuba Research Center, AIST
-
Sato Masahito
National Chemical Laboratory For Industry
-
Fujiwara Ichiro
National Chemical Laboratory For Industry
-
Shin Shigemitsu
National Chemical Laboratory for Industry
関連論文
- 一様直流電場印加時の複合液滴の挙動に関する理論及び実験的研究
- 2-ブロモデカン酸による混合溶液中からのGaの抽出に及ぼす共存Alの影響
- 複合液滴の挙動に及ぼす直流電場の影響
- 一様直流電場下での誘電性液体中の液滴の挙動
- 疎水性空間を有するコーン型ホルミルニトロカリックス[4]アレーンの合成
- Measurement of Thermal Diffusivity of Nonlinear Optical Polymer Thin Films Using Photoacoustic Method
- EFFECT OF EHD CONVECTION ON MOTION OF A BUBBLE UNDER MICROGRAVITY
- Electrochemical Oxidation of Methane to Synthesis Gas Using an Oxide Ionic Conductor (論文特集号 電解科学技術の進展)
- Catalytic Methanol Decomposition at Low Temperature over Pd Catalyst Derived from Mesoporous Silica Carried Pd-Hydrotalcite
- KINETIC STUDY OF FURFURAL FORMATION ACCOMPANYING SUPERCRITICAL CARBON DIOXIDE EXTRACTION
- Novel Carbon Molecular Sieve Membranes Derived from Poly(phenylene oxide) and Its Derivatives for Gas Separation
- 2-ブロモデカン酸を用いた乳化液膜法によるGaの抽出に及ぼす共存物質の影響
- ADSORPTION OF WATER VAPOR ON SEPIOLITE FOR CHEMICAL HEAT PUMPS
- The steam stability of H-ZSM-5-type zeolites containing alkaline earth metals.
- Adsorption properties of high-silica zeolites for high-temperature chemical heat pumps.
- Phase Equilibrium Study of Extraction and Concentration of Furfural Produced in Reactor Using Supercritical Carbon Dioxide
- A new catalyst for the low temperature oxo process with the characteristic of easy separation.
- High resolution 29Si nuclear magnetic resonance study on gallosilicates with zeolitic structures.
- Crystallographic Properties of Ca2Fe2O5. Difference in Crystallographic Properties of Brownmillerite-like Compounds, Ca2Fe2O5 and Sr2Fe2O5, at Elevated Temp
- A study of inorganic ion-exchangers. VIII. The synthesis of the crystalline Zr(RNH)xH2-x(PO4)2yH2O and their characteristics(R=(CnH2n+1)3 and C5H5, n=1-6).
- The long-term testing of ZSM-5-type zeolite containing strontium for the high-temperature conversion of methanol to olefin.