非関連型のDmcker-Prager弾塑性体の漸近解を使用した最大摩擦せん断応力破壊基準によるせん断破壊の考察
スポンサーリンク
概要
- 論文の詳細を見る
A new fracture criterion of the shear failure for the geomaterials is presented which predicts a straight extension of a crack in an elastic plastic material under compressive loads called "The maximum frictional shear stress criterion". Weexamine the criterion by using both the singular and the constant terms in the asymptotic expansion of the crack tip stress fields for a non-associate linear hardening Drucker-Prager elastic-plastic material. As a result, we find that the confining pressure, the friction along the crack surfaces, the internal material friction, and the dilatancy effect are the lowering of the extensive hoop stress: Then they cause the maximum frictional shear stress to extend a crack straight
- 土木学会 = Japan Society of Civil Engineersの論文
土木学会 = Japan Society of Civil Engineers | 論文
- 鉄筋腐食によって損傷を受けたRCばりの挙動に関する考察
- 鋼繊維-セメント系マトリックス間の付着破壊進展機構と鋼繊維補強モルタルの高靭性化
- ケーソン護岸連結目地内での流体共振特性に及ぼす入射角の影響
- き裂を有する線形異方弾性体の圧縮荷重下における応力・変位の荷重履歴依存性
- 路面補修前後の長期モニタリングから評価した周期性路面の橋梁に及ぼす影響