Glass transition temparature for polyvinyl chloride was measured by high pressure DTA method over 15 to 250 MPa. The transition temperature at a measuring pressure was determined from a heating run of 16 K/min after the sample has been glassified with the same rate at the pressure. The relationship of T_g against P was analyzed by the Simon-type equation and initial slope of the pressure dependence of T_g was given 18 K/100 MPa. The present thermal data and the dilatometric data, previously reported, show a similar pressure dependence. The difference in temperature for these data may be ascribed to time dependence. This fact may indicate that there is no preference for both entropic and volumetric factors to govern glass transition temperature. Detailed description of the instrument is also given.
- 九州大学大学院総合理工学研究科の論文
- 1985-01-01
九州大学大学院総合理工学研究科 | 論文
- 汎用マイクロプロセッサを用いたDatarol-IIプロセッサエレメントにおける細粒度スレッド処理機構
- 体積法による高圧下のガラス転移の研究
- Synthesis of 3,4-Dibromo-2,5-bis-substituted Thiophenes
- Reaction of 3a, 5, 6a-Tripheny1-3, 3a-dihydro-2H-furo[3,2-b]-pyrrole-2,6 (6aH)-dione with Hydrazine, Phenylhydrazine, and Benzoylhydrazine
- Pressure Effect on the Cycloaddition of Tropone to 2,3-Dihydrofuran