炭化タンタルの高温変形挙動
スポンサーリンク
概要
- 論文の詳細を見る
High-temperature deformation behavior of tantalum carbide, TaC_<0.78>, prepared by the floating zone technique with radio-frequency induction heating, is investigated. It is found that the crystals become appreciably ductile above 1600 K and exhibit a marked work softening phenomenon, which is characteristic of covalent-bonded crystals such as Ge and Si. The phenomenon becomes less clear with decreasing strain rate. The mechanical equation of state at the yield stress can be expressed by ε^^・_P＝A(σ_y/E(^mezp(-Q/(RT)), where m＝3.8 and Q＝370 kJ/mol in the temperature range 1600 to 2320 K. The value of Q is close to the activation energy for carbon diffusion in TaC.
- 九州大学大学院総合理工学研究科の論文
- 1982-06-30
九州大学大学院総合理工学研究科 | 論文
- 汎用マイクロプロセッサを用いたDatarol-IIプロセッサエレメントにおける細粒度スレッド処理機構
- 体積法による高圧下のガラス転移の研究
- Synthesis of 3,4-Dibromo-2,5-bis-substituted Thiophenes
- Reaction of 3a, 5, 6a-Tripheny1-3, 3a-dihydro-2H-furo[3,2-b]-pyrrole-2,6 (6aH)-dione with Hydrazine, Phenylhydrazine, and Benzoylhydrazine
- Pressure Effect on the Cycloaddition of Tropone to 2,3-Dihydrofuran