湿式ボールミル法を用いた無機性産業廃棄物の再資源化技術の開発
スポンサーリンク
概要
- 論文の詳細を見る
The possibility of material recycling of inorganic slag by wet ball milling with distilled water and an ethylenediaminetetraacetic acid disodium salt dehydrate (EDTA·2Na·2H2O) reagent was investigated. The wet ball milling of the simulated waste slag powder was performed using a ball mill pot and balls in air for 10 - 100 h at room temperature with the rotational speed fixed at 200 rpm. The fractions of CaO and Fe2O3 in the specimens obtained by wet-ball-milling the simulated waste slag powder decreased, that of SiO2 increased, and those of Al2O3 and Na2O hardlychanged. These specimens contained 0.1 – 0.8mass% ZrO2. Appropriate solution and time for wet ball milling were 300 ml distilled water and 20 h, respectively. When the wet ball milling of the simulated waste slag powder was performed twice, the fractions of CaO, Al2O3 and Fe2O3 in the specimen obtained after repeated wet ball milling decreased, those of SiO2 and ZrO2 increased and that of Na2O hardly changed in comparison with those in the specimen wet-ball-milled once. The insoluble end product obtained by soaking the specimen wet-ball-milled once in 6M HCl for 20 hours was composed of 98.5mass% SiO2 and 0.6mass% or less other oxides and is usable as glass material.
論文 | ランダム
- 150 移植薄筋を用いた肛門機能再建に関する基礎的研究(第45回日本消化器外科学会総会)
- V2-10 胸腔鏡下食道切除術のpitfallと安全対策(腹腔鏡下手術のpitfall)
- 15. 術前FEC療法によりpCRの得られた1例 ―投与期間および手術時期についての考察―(第40回埼玉・群馬乳腺疾患研究会)
- P-3-179 S状結腸癌術後比較的早期に発症した難治性虚血性腸炎の1例(大腸合併症,一般演題(ポスター),第63回日本消化器外科学会総会)
- O-2-10 大腸癌と鑑別困難であった腸結核の1例(小腸 炎症性疾患,潰瘍,一般演題(口演),第62回日本消化器外科学会定期学術総会)