Crystallization and magnetic property of iron oxide nanoparticles precipitated in silica glass matrix
スポンサーリンク
概要
- 論文の詳細を見る
Crystallization and magnetic property of Fe2O3 nanoparticle precipitated in SiO2 matrix was investigated. Fe2O3/SiO2 nanocomposite thin film was obtained by annealing of the amorphous Fe-Si-O thin film deposited by RF-magnetron sputtering of (α-Fe2O3)_[1-x]/(SiO2)x composite targets. The Fe2O3 crystallite size increased with decreasing SiO2 area ratio, x of the target and increasing annealing temperature ε-Fe2O3 with the crystallite size of 20~30 nm was obtained after annealing the film deposited in SiO2 area ratio, x = 0.33~0.42 at 900℃. Lower SiO2 area ratio (x) than 0.25 and higher annealing temperature resulted in precipitation of α-Fe2O3 with the larger crystallite size than 40 nm. In the case of SiO2 area ratio, x ≥ 0.50, the annealed film was amorphous and showed higher magnetization and smaller coercivity due to the precipitation of very small crystalline γ-Fe2O3. The ε-Fe2O3/SiO2 composite thin film showed ferromagnetic hysteresis with coercive force of 0.14 T.
論文 | ランダム
- 硬水がコンクリートの諸強度に及ぼす影響に関する基礎的研究
- 訪問看護制度の変遷 (焦点 訪問看護の現状とグランドデザイン)
- 文身抹消術に関する研究-1-
- 北海道における草地開発の全容 (わが国における草地開発の可能性(特集))
- Properties of the Proteinase from a Luminous Bacterium, Vibrio splendidus ATCC 33125