熱サイクル疲労後の遮熱コーティングの残存密着強度に及ぼすボンドコート界面粗さの影響(<小特集>ガスタービン用遮熱/耐環境コーティング技術)
スポンサーリンク
概要
- 論文の詳細を見る
The effect of the bond coat on residual adhesion strength after thermal cycle fatigue was investigated in plasma-sprayed thermal barrier coatings (TBC). This study used CoNiCrAlY powder with two different particle sizes for spraying bond coat material to examine the effect of interface roughness between the bond coat and top coat. In addition, the bond coat was sprayed on either by a high velocity oxy-fuel (HVOF) or a low pressure plasma spray (LPPS). The residual adhesion strength of the TBC top coat was evaluated as a function of the number of thermal cycles by the modified 4-point bending test. In addition, SEM observations of thermal fatigue cracking morphologies and measurements of the residual stress in the ceramic top coat were carried out. The experimental results indicated that, after thermal cycle fatigue, microcracks were generated in the ceramic top coat; however, they were moderated in a rough interface TBC compared to a smooth interface TBC. In addition, the bond coat sprayed by the HVOF method showed a higher resistance to microcracking than the coat sprayed using the LPPS. Residual stress in the ceramic top coat is almost zero at 0 thermal cycles. After thermal cycle fatigue, it becomes compression; however, it is independent of the bond coat. There was little difference in the adhesion strength by bond coat in as-sprayed conditions. On the other hand, the specimen with a rough interface exhibited higher residual adhesion strength after thermal cycle fatigue compared with the specimens with a relatively smooth interface. In addition, if the bond coat is sprayed by HVOF, the residual adhesion strength increases. It was revealed that the difference in residual adhesion strength by bond coat is related to the distribution morphology of thermal fatigue microcracks.
論文 | ランダム
- 全日本空輸社長 大橋洋治 たとえば温泉文化や沖縄など、海外の人に知られていない日本の魅力を訴えていきたい (特集 観光立国こそが内需喚起の切り札) -- (私の観光立国 提言)
- テロ、JAL・JAS統合の荒波の中 全日本空輸社長 大橋洋治--タブーはかなぐり捨てて改革を推し進める
- 全日空が突然の社長交代 野村吉三郎が復配一歩手前で退陣した理由〔含:インタビュー 全日本空輸新会長 野村吉三郎/全日本空輸新社長 大橋洋治〕
- ビニルピリジン-ビニルビピリジン共重合体型〔Ru(bpy)3〕2+錯体の合成と光化学的性質(ノ-ト)
- 光感応性高分子修飾電極を用いる光センサ(ノ-ト) (センサ開発と高分子)