SP-700/SCS-6チタン合金複合材とモノリシックなマトリックス材の低サイクル疲労破壊挙動の相違
スポンサーリンク
概要
- 論文の詳細を見る
The isothermal low cycle fatigue (LCF) fracture behavior of a new generation titanium alloy matrix composite, SP-700/SCS-6, were investigated compared with the monolithic matrix alloy. To study the effects of the test temperature and the loading frequency on the LCF fracture behavior in SP-700/SCS-6, the LCF tests were performed under strain-controlled condition at room temperature and 450℃. In the LCF tests two strain wave shapes were applied : the fast-fast wave in which the loading frequency was 0.5 Hz, and the slow-slow wave in which it was 1/360 Hz, respeetively. The conclusions obtained from the experimental results are summarized as follows : (1) The LCF lives of the composite were almost comparable to those of the matrix alloty, on the basis of strain range. In other words, the performace of the present composite material can be absolutely improved, since the stiffness and the deformation resistance can significantly increased by the composition. (2) The fatigue cracks were initiated from the matrix part at the specimen corner. The fiber pull-out was not so significant on the fracture surface. (3) The LCF lives of the composite at 450℃ were longer than those at room temperature. This trend was in contrast to the monolithic matrix alloy which exhibits a normal temperature dependence in the LCF lives. (4) The LCF lives of the composite under the slow-slow wave was noticeably shorter than those under the fast-fast wave at high temperature. This trend was familiar to the conventional monolithic materials.
論文 | ランダム
- 超音波気管支鏡(EBUS-TBNA・GS)(気管支鏡セミナーより)
- 実技のABC:映画レンズ・カメラのマウント--映画用レンズマウント・カメラマウント及びフランジバック(レンズ取り付け部からフィルム面までの距離・寸法)の変遷
- UHFテレビジョン放送アンテナへのパッチアンテナの応用に関して
- パッチアンテナを用いたテレビジョン放送アンテナ
- 1/2波長パッチアンテナの入力インピーダンス特性について