抵抗ろう接したチタン合金継手の引張強さの分布に及ぼすろう材の影響
スポンサーリンク
概要
- 論文の詳細を見る
Ti-l0mass%Zr alloy was resistance brazed using two brazing filler metals, silver and copper. To investigate the effect of brazing filler metal on the distribution of the tensile strength of joints, their tensile strength and fracture surface were examined. The set of the tensile strength of joints resistance-brazed with silver has the sample mean of 422MPa and the sample standard deviation of 31MPa, while that of joints resistance-brazed with copper has the sample mean of 431MPa and the sample standard deviation of 62MPa. The tensile strength of joints resistance-brazed with silver and copper, δB[MPa],are expressed with the area fraction of ductile fracture surface, Αd, as: σB=211Αd+300 for silver and σB= 584Ad+ 178 for copper. The sample standard deviations of the two sets are discussed on the basis of the slopes and intercepts of the equations connecting σB and Ad.
- 福井大学工学部の論文
福井大学工学部 | 論文
- 周期補正型繰返し制御法の提案--レピア式よこ糸挿入機構への適用を例として
- 中性子・ガンマ線を同時利用した産業用密度計の研究
- ガンマ線散乱を利用した産業用レベル計測の研究
- 滑り周波数制御方式による誘導電動機のベクトル制御の2次抵抗温度変化の一補償法
- PWM制御アクティブフィルタの非干渉化2自由度制御法とその特性