Effect of Principal Direction Change on High Temperature Multiaxial Low Cycle Fatigue Lives Using Cruciform Specimen
スポンサーリンク
概要
- 論文の詳細を見る
Low cycle fatigue tests were carried out using crucifonn specimens of Type 304 stainless steel under multiaxial strain states at 823K. Strain paths employed in the tests were not only proportional strain histories but also severe strain histories including out-of-phase strain in order to examine the effect of stain history on multiaxial fatigue life. The crack mode was also discussed by observing the crack direction on specimen surface. For the crucifonn specimen, the principal strain axes are always fixed but the maximum principal strain direction is changed into the one of three principal strain axes due to the severe strain histories. The change in direction of the maximum principal strain from one principal axis to the others had no effect on fatigue life because the additional interaction between slip systems did not occur resulting in no large additional hardening. Only the strain multiaxiality influenced the fatigue life which can be predicted as well as the multiaxial fatigue life under proportional strain histories. The strain history also did not influence the mode of crack initiation.
- 福井大学工学部の論文
福井大学工学部 | 論文
- 周期補正型繰返し制御法の提案--レピア式よこ糸挿入機構への適用を例として
- 中性子・ガンマ線を同時利用した産業用密度計の研究
- ガンマ線散乱を利用した産業用レベル計測の研究
- 滑り周波数制御方式による誘導電動機のベクトル制御の2次抵抗温度変化の一補償法
- PWM制御アクティブフィルタの非干渉化2自由度制御法とその特性