Enhancement of thermoelectric efficiency in type-VIII clathrate Ba8Ga16Sn30 by Al substitution for Ga
スポンサーリンク
概要
- 論文の詳細を見る
Single-crystalline samples of type-VIII clathrate Ba8Ga16-xAlxSn30 (0 <= x <= 12) were grown from Sn flux to characterize the structural and thermoelectric properties from 300 to 600 K. The lattice parameter increases by 0.5% as x is increased to 10.5 whose value is the solubility limit of Al. The Seebeck coefficients of all samples are largely negative and the absolute values increase to approximately 300 mu V/K on heating to 600 K. This large thermopower coexists with the metallic behavior in the electrical resistivity. The values of resistivity for 1 <= x <= 6 at 300 K are in the range 3.3-3.8 m Omega cm which is 70% of that for x=0. As a result, the power factor for x=4 and 6 has a rather large maximum of 1.83 x 10(-3) W/m K-2 at 480 K. The thermal conductivity stays at a low level of 0.72 W/mK up to 480 K, and the sample with x=6 reaches a ZT value of 1.2 at 500 K.
- 2010-10-07
論文 | ランダム
- 江戸時代前期の禁裏における冷泉家本の書写活動について
- 禁裏・宮家・公家文庫収蔵古典籍のデジタル化による目録学的研究 (史料研究) -- (科学研究費・委任経理金等による研究)
- 資料紹介 広橋綱光『禁裏晴蹴鞠記』・二条持通『於禁裏晴御鞠記』
- 後土御門天皇期の禁裏における猿楽興行の諸様相--公家集団の申沙汰を中心に
- 室町後期・戦国期の内侍所