Nanocrack Formation in Hematite through the Dehydration of Goethite and the Carbon Infiltration from Biotar
スポンサーリンク
概要
- 論文の詳細を見る
The cracks in nano-order are generated and propagated when the combined water is released during the dehydration. If the nanopore can be utilized for a reaction site, the overall reaction can be extremely accelerated. On the other hand, it is well known that woody biomass is an attractive alternative fuel for the reduction of CO2 emission. However, the process of biomass pyrolysis is disturbed by the tar which causes a clogging in gas tubing system. Hata et al. found that the tar was consumed almost 100% in the iron ore layer having nanocrack or nanopore. The nanocracks formed in hematite crystals after dehydration of goethite were about 4 nm in width, which is in excellent agreement with the result of BET measurement. When the carbon deposited from tar into the nanocracks, reduction reactions were occurred simultaneously. The deposited carbons completely infilled into the nanocracks and the void in the sample.
論文 | ランダム
- A New Method of Synthesis of Alkyl β-Glycosides Using Sucrose as Sugar Donor
- Enzymatic Synthesis of α-Anomer-Selective D-Glucosides Using Maltose Phosphorylase
- 21446 常時微動データに基づく鉄筋コンクリート造高層煙突の振動振幅と減衰特性
- 21436 常時微動測定に基づく鉄骨造高層建物の高次モードの減衰特性
- 2003 振動測定に基づく鉄骨造高層建物の減衰特性に関する研究 : 各次モードの減衰定数および振動振幅が減衰定数に与える影響