Formation of porous anodic titanium oxide films in hot phosphate/glycerol electrolyte
スポンサーリンク
概要
- 論文の詳細を見る
The present study reveals the formation of porous anodic films on titanium at an increased growth rate in hot phosphate/glycerol electrolyte by reducing the water content. A porous titanium oxide film of 12 mu m thickness, with a relatively low content of phosphorus species, is developed after anodizing at 5 V for 3.6 ks in 0.6 mol dm(-3) K2HPO4 +0.2 mol dm(-3) K3PO4/glycerol electrolyte containing only 0.04% water at 433K. The growth efficiency is reduced by increasing the formation voltage to 20V, due to formation of crystalline oxide, which induces gas generation during anodizing. The film formed at 20V consists of two layers, with an increased concentration of phosphorus species in the inner layer. The outer layer, comprising approximately 25% of the film thickness, is developed at low formation voltages, of less than 10 V, during the initial anodizing at a constant current density of 250 A m(-2). The pore diameter is not significantly dependent upon the formation voltage, being similar to 10 nm. (C) 2010 Elsevier Ltd. All rights reserved.
- 2010-04-30
著者
-
Habazaki H
Institute For Materials Research Tohoku University
-
Habazaki H.
Graduate School Of Engineering Hokkaido University
関連論文
- Formation of porous anodic titanium oxide films in hot phosphate/glycerol electrolyte
- ニオブおよびタンタルのアノード酸化
- 熱可塑性樹脂とマグネシウム塩混合物からの賦活処理を経ないメソポーラスカーボンの調製
- アルミニウムのアノード酸化
- 番外編 ユーザーの立場に立った表面分析の新展開(番外・最終回)FIBとrf-GD併用による半導体素子断面試料の作成--完璧なSEM-friendly surfaceを求めて
- 超ミクロトームによる断面出しと低加速・高分解能反射電子像観察
- 番外編 ユーザーの立場に立った表面分析の新展開(番外6)超高分解能BSE imagingによる高純度Al箔表面のPbナノ微粒子の観察
- 電子顕微鏡による断面・界面観察の新たな世界
- 高分解能FE-SEM/ESB/ASBの拓く : 新たなナノ表面分析の世界
- バルブ金属アノード酸化皮膜の結晶化