POLYMERIZATION OF o-VINYLPHENOL
スポンサーリンク
概要
- 論文の詳細を見る
The structure of the polymer of o-vinylphenol was studied. o-Vinylphenol(o-VP) was prepared by thermal decarbonization of o-cumaric acid which was obtained by hydrolysis of cumarin with sodium ethylate. Free radical and cationic polymerization of o-VP were carried out in bulk or in CH2Cl2 solution by using BPO, AIBN, BF3･OEt2, AlCl3, and TiCl4 as initiator. The polymers were reprecipitated by water from methanol solution and residual monomer was removed with dilute aqueous alkaline solution. The resulting polymers were white powder or viscous materials. The structure of the polymers were investigated by UV, IR, and NMR spectral measurement. UV spectra showed that the polymers have similar structures except for the one prepared by using BF3･OEt2. IR spectra showed the presence of methyl group and 1,2,4-trisubstituted benzene structure which are not expected from ordinary vinyl polymerization mechanism. The relative intensities of -CH3 and -CH2 group differ among polymers and suggested only the polymer prepared by using AIBN had relatively few -CH3 group. NMR spectral study supportedthe results obtained from IR spectra. The presence of -CH3 group was confirmed by C-methyl determination method (chromic acid oxidizing method) and the the amounts of C-CH3 groups were determined. From these results it was concluded that o-VP polymerizes through two different propagation steps, one is ordinary vinyl polymerization mechanism and the other the addition of vinyl group to pheno1ic nuclei.
論文 | ランダム
- 尾張のお鍬祭りについて (特集 平成の御鍬祭) -- (全体を見渡して)
- 大腿に発症したRippled-Pattern Sebaceomaの1例 (特集 毛嚢系腫瘍)
- Raynaud 現象に対するミオナール^【○!R】の効果 : サーモグラフィーによる検討
- 結核菌系抗原抗体反応
- 結核の不完全抗体の研究と新しい不完全抗体証明法について