Class I Gap-formation in Highly-viscous Glass-ionomer Restorations: Delayed vs Immediate Polishing
スポンサーリンク
概要
- 論文の詳細を見る
<p>This in vitro study evaluated the effects of delayed versus immediate polishing to permit maturation of interfacial gap-formation around highly viscous conventional glass-ionomer cement (HV-GIC) in Class I restorations, together with determining the associated mechanical properties. Cavity preparations were made on the occlusal surfaces of premolars. Three HV-GICs (Fuji IX GP, GlasIonomer FX-II and Ketac Molar) and one conventional glass-ionomer cement (C-GIC, Fuji II, as a control) were studied, with specimen subgroups (n=10) for each property measured. After polishing, either immediately (six minutes) after setting or after 24 hours storage, the restored teeth were sectioned in a mesiodistal direction through the center of the model Class I restorations. The presence or absence of interfacial-gaps was measured at 1000× magnification at 14 points (each 0.5-mm apart) along the cavity restoration interface (n=10; total points measured per group = 140). Marginal gaps were similarly measured in Teflon molds as swelling data, together with shear-bond-strength to enamel and dentin, flexural strength and moduli. For three HV-GICs and one C-GIC, significant differences (p<0.05) in gap-incidence were observed between polishing immediately and after one-day storage. In the former case, 80–100 gaps were found. In the latter case, only 9–21 gaps were observed. For all materials, their shear-bond-strengths, flexural strength and moduli increased significantly after 24-hour storage.</p>
論文 | ランダム
- 3P198 クラミドモナス鞭毛内腕ダイニンcの微小管の負電荷領域から受ける影響および微小管に沿った一次元ブラウン運動(分子モーター)
- 1SB03 高速AFMによるダイニン・ミオシンVのダイナミクス観察(分子モーター研究の新潮流)
- 1SB01 鞭毛ダイニンの1分子観察と構造変化(分子モーター研究の新潮流)
- エバネセント光励起による単一蛍光分子観察における励起光偏光の影響
- 138K中間鎖のリン酸化によるクラミドモナス両腕ダイニンfの構造変化