n-アルカンの結晶化における高温構造の凍結
スポンサーリンク
概要
- 論文の詳細を見る
The freezing-in phenomena of high temperature structures for solution-crystallized samples of dopentacontane (abbr. as C52), henpentacontane (C51), tetratetracontane (C44) and tritetracontane (C43) were studied by using DSC, X-ray diffraction and SEM. C52 and C44 were crystallized as monoclinic and C51 and C43 as orthorhombic. These crystals transformed before melting to oblique structures. After annealing at these temperature regions, the crystal morphologies changed, indicating that the oblique structures were frozen-in. The structure of C52 was determined as monoclinic P21/a. It is noted that this crystalline feature of evennumber n-alkanes holds still at the mobile high temperature phase.
- 九州大学大学院総合理工学研究科の論文
- 1992-09-01
九州大学大学院総合理工学研究科 | 論文
- 汎用マイクロプロセッサを用いたDatarol-IIプロセッサエレメントにおける細粒度スレッド処理機構
- 体積法による高圧下のガラス転移の研究
- Synthesis of 3,4-Dibromo-2,5-bis-substituted Thiophenes
- Reaction of 3a, 5, 6a-Tripheny1-3, 3a-dihydro-2H-furo[3,2-b]-pyrrole-2,6 (6aH)-dione with Hydrazine, Phenylhydrazine, and Benzoylhydrazine
- Pressure Effect on the Cycloaddition of Tropone to 2,3-Dihydrofuran