Thermal conductivity of single and multi-stacked DI-BSCCO tapes
スポンサーリンク
概要
- 論文の詳細を見る
We have measured the temperature dependence of the thermal conductivity, κ(T), for DI-BSCCO® tapes fabricated by Sumitomo Electric Industries, Ltd., which are (Bi,Pb)2Sr2Ca2Cu3O8+x tapes sheathed with Ag or Ag–Au alloy. The κ(T) of the tape sheathed with Ag (residual resistance ratio (RRR) = 15) decreases with decreasing temperature and starts to increase rapidly below 60 K, with a maximum at around 15 K. On the other hand, the κ(T) of the tape sheathed with Ag–5.4 wt%Au alloy has a very low value that decreases monotonically with decreasing temperature. At around 77 K, the absolute values of κ(T) for both tapes were about and , respectively. The κ(T) of a stacked sample, in which six DI-BSCCO tapes sheathed with Ag are soldered, was also measured. The measured κ(T) was fairly well reproduced by the estimated κ(T), which was calculated using the measured κ(T) of the single tape and solder.http://www.elsevier.com/wps/find/journaldescription.cws_home/30407/description#description
論文 | ランダム
- Block Spin Transformations of Random Walks and Analytic Domain of the Free Energy of the N Vector Model (場の理論の共通課題)
- 鋼桁パネルのせん断耐荷力の簡易予測について(工学)
- 応力性状から見た鋼桁パネルのせん断耐荷力について(工学)
- 荷重・変位挙動から見たせん断桁パネルの耐荷力特性
- せん断力を受ける桁パネルの非弾性交番座屈試験