Quantifying carbide particles in steel by image processing method
スポンサーリンク
概要
- 論文の詳細を見る
SR embrittlement srises in HAZ of 2 1/4Cr-1Mo steel by the long-time reheating in SR treatment. The behavior of carbide particle seems to have close relation with SR embrittlement, as they grow significantly in the time range of SR embrittlement. The number of carbide particles which observed on the fracture surface of the specimen suffered from SR embrittlement is larger than that in cross-section. The systematic investigations may be needed to discuss the role of carbide particles on SR embrittlement. In this study, the size and shape of carbide particle were measured systematically by using the image processing. The experimental system for quantifying of carbide particles is combined with scanning electron microscope (SEM) and a personal computer. The suitable method of image processing which can recognize the shape of carbide particles in the image by SEM was established in the fast place. The size of carbide particle in cross-section increased with an increasing time of SR treatment. The shapes of carbide particles in cross-section changed from sphere to elliptical with the growth of particle. But the relation between the size and shape of carbide which was observed on fracture surface was different from that in cross-section when SR embrittlement occurs significantly. The fractured carbide particles were observed on fracture surface. This result suggests that the crack propagation in carbide particles helps to occur SR embrittlement.
- Faculty of Engineering, Mie Universityの論文
- 2000-12-27
Faculty of Engineering, Mie University | 論文
- Approximate Method of Elastic Buckling Strength Analysis for Irregular Frames
- Elastic Buckling Strength of Steel Frames Connected to Core Wall
- Calculations of Energy Shift of the Conduction Band-Edge in Doped and Compensated GaP
- Estimation of the Glass Transition Pressure of Liquids under Very High Pressure by Viscoelastic Analysis
- Information Extraction from Electronic Mail