Chemical Diffusion in the Iridium-Rich A1 and L12 Phases in the Ir-Nb System
スポンサーリンク
概要
- 論文の詳細を見る
The diffusion in iridium-rich Ir-Nb alloys has been studied by single-phase interdiffusion experiments. The chemical diffusion coefficient has been measured for the primary fcc solidsolution and the L12 ordered compound Ir3Nb in the temperature range between 1650 and 1950 °C, using Ir/Ir-8Nb and Ir-26Nb/Ir-28Nb diffusion couples, respectively (numbers indicate mol%). While the chemical diffusion coefficient in the solid-solution phase is close to the tracer self-diffusion coefficient of pure iridium, the diffusion in the compound phase is extremely slow: the chemical diffusion coefficient is 1⁄40 to 1⁄50 of that in the solid solution. The low diffusion rate in the compound must be beneficial for high-temperature performance of refractory superalloys based on the Ir-Nb system.
論文 | ランダム
- 9344 郊外大規模ショッピングセンターの構えにおける建築的特徴(意匠論・構成(1),建築歴史・意匠)
- 自動車の取り扱いからみた住宅の構えと住宅地の街並み : 世田谷区奥沢を事例として
- 9343 キャットストリート周辺地域における建築条件の変遷 : キャットストリート周辺地域における建築条件の変遷と建築物の種類(1)(意匠論(3):都市(1),建築歴史・意匠)
- 薬剤性間質性肺炎への対策--臨床研究・疫学研究でわかってきたこと (特集 肺癌生存期間延長の謎--今何が起こっている?) -- (肺癌治療における副作用対策)
- シンポジウム紹介 第3回国際化学療法学会癌治療総会