Depth profile high-energy spectroscopic study of Mn-doped GaN prepared by thermal diffusion
スポンサーリンク
概要
- 論文の詳細を見る
We have performed an in situ depth profile study of Mn-doped GaN prepared by a low temperature thermal diffusion method using photoemission and x-ray absorption spectroscopy. It was revealed from the core-level photoemission measurements that Mn ions are diffused into a deep (∼70 Å) region of the GaN substrates and that the line shapes of Mn 3d partial density of states obtained by resonant photoemission measurements were close to that of Ga1-x Mnx N thin films grown by molecular-beam epitaxy. From x-ray absorption spectroscopy and x-ray magnetic circular dichroism measurements at the Mn L edge, it was revealed that the doped Mn ions were in the divalent Mn2+ state and primarily paramagnetic. In magnetization measurements, weak hysteresis was detected in samples prepared using p -type GaN substrates while samples using n -type GaN substrates showed only paramagnetism.
- 2007-05-22
論文 | ランダム
- 異時発生両側睾丸腫瘍の1例(第458回東京地方会)
- 両側褐色細胞腫の1例(第452回東京地方会)
- 経腹的超音波断層法による前立腺容量の術前推定法について
- 経腹的超音波診断法による前立腺容量の推定法について : 第51回東部総会
- 救命ICUにおける急性腎不全の検討 : 第50回東部総会