Partial oxidation of propane to synthesis gas over noble metals-promoted Ni/Mg(Al)O catalysts : High activity of Ru-Ni/Mg(Al)O catalyst
スポンサーリンク
概要
- 論文の詳細を見る
Effect of the addition of small amount of noble metal, i.e. Ru, Rh, Pd, Ir or Pt, in the Ni/Mg(Al)O catalyst on the catalytic activity for the partial oxidation of propane has been investigated. Mg2.5(Ni0.5)-Al hydrotalcite was prepared by co-precipitation and was calcined to form Mg2.5(Al,Ni0.5)O periclase. When the powders of the periclase were dipped in an aqueous solution of the nitrate of Ru(III), Rh(III), Pd(II), Ir(III) or Pt(II), a reconstitution of the hydrotaclite took place on the surface of Mg2.5(Al,Ni0.5)O particles due to a "memory effect." The calcination followed by the reduction of the dipped samples produced highly dispersed noble metal-Ni supported catalysts. The loading of noble metal gave rise to a decrease in the reduction temperature of Ni2+ to Ni0 on Mg2.5(Al,Ni0.5)O periclase, an increase in the amount of H2 uptake on the Ni metal and moreover a decrease in the particle size of Ni metal formed on the noble metals-Ni/Mg2.5(Al)O catalyst. When the noble metals-Ni0.5/Mg2.5(Al)O catalysts were tested in the temperature-cycled operation of propane partial oxidation between 400 ºC and 700 ºC, the deactivation due to both Ni oxidation and coke formation on the catalyst was effectively suppressed by the loading of noble metals. The combination of Ru and Ni0.5/Mg2.5(Al)O was the most effective; the high sustainability against both Ni oxidation and coke formation was obtained only with 0.1 wt% of Ru loading. A dipping of 1.0 g of the powders of Ni0.5/Mg2.5(Al)O periclase in a 5 ml of Ru(III) nitrate-aqueous solution was enough to reconstitute the hydrotalcite on the surface of the powder particles, leading to the formation of the Ru-Ni bimetal loaded catalyst with the high activity as well as the high sustainability.
論文 | ランダム
- Damage Maps for Layered Ceramics under Simulated Mastication
- Sliding Contact Fatigue Damage in Layered Ceramic Structures
- 鋼繊維補強コンクリ-トとその道路舗装への応用
- STUDIES ON P WAVES OF THE SPATIAL MAGUNITUDE ECG IN IDIOPATHIC CARDIOMYOPATHY : Myocardial Disease (II) : FREE COMMUNICATIONS (II) : PROCEEDINGS OF THE 49th ANNUAL SCIENTIFIC MEETING OF THE JAPANESE CIRCULATION SOCIETY
- 企業スケッチ 株式会社高島屋--全社員意識調査で課題を把握、各部署ごとに課題の改善に取り組み男女共同参画型企業を目指す