A-1 リン酸塩系埋没材の硬化・加熱過程での気孔率(鋳造・金属材料,一般講演(口頭発表),第59回日本歯科理工学会学術講演会)
スポンサーリンク
概要
- 論文の詳細を見る
Because porosity is an effective factor for determining the strength, setting/heating expansion, and permeability of the compacts at casting, the porosity of commercial available phosphate-bonded investments for set and heated compacts was measured and theoretically computed quantitatively. The experimentally measured porosities for the set and burnout investments were about 24-32% for dry set compacts and 42-45% for burnout compacts, which well agreed with the numerically computed results. Procedure developed in this study is helpful to estimate the porosity of the set and the burnout investment compacts with various amount of mixing liquid for various compositional investment powders.
- 2012-03-25
著者
関連論文
- P-91 Ni-Ti合金及びステンレス鋼の腐食生成物のXAFS分析(チタン・鋳造・腐食,一般講演(ポスター発表),第54回日本歯科理工学会学術講演会)
- 昇温脱離分析によるチタンの侵食に対する酸化膜の働きの評価
- チタンの侵食と酸化被膜の働き(チタン, 創立55周年記念大会平成17年春期 (東京) 第45回日本歯科理工学会学術講演会)
- P-54 スペースホルダー法を用いた医用チタン多孔体の気孔径制御(金属材料,一般講演(ポスター発表),第59回日本歯科理工学会学術講演会)
- A-1 リン酸塩系埋没材の硬化・加熱過程での気孔率(鋳造・金属材料,一般講演(口頭発表),第59回日本歯科理工学会学術講演会)
- P-5 石膏系埋没材とリン酸塩系埋没材の硬貨・加熱過程での気孔率の比較(研究奨励賞応募ポスター発表,第59回日本歯科理工学会学術講演会)
- P-31 Au-Pt合金の磁化率への組成,加工および熱処理の影響(歯科用合金・チタン,一般講演(ポスター発表),第60回日本歯科理工学会学術講演会(創立30周年記念大会))
- P-30 医療用非磁性Au-Pd基合金の開発 : Au-Pd合金の磁化率と機械的特性(歯科用合金・チタン,一般講演(ポスター発表),第60回日本歯科理工学会学術講演会(創立30周年記念大会))
- P-67 リン酸塩系埋没材の硬化,加熱後の気孔率への混和液のコロイダルシリカ濃度の影響(ジルコニア・陶材・セメント・埋没材,一般講演(ポスター発表),第60回日本歯科理工学会学術講演会(創立30周年記念大会))
- Au-Pt合金の磁化率への組成, 加工および熱処理の影響
- リン酸塩系埋没材の硬化, 加熱後の気孔率への混和液のコロイダルシリカ濃度の影響
- 医療用非磁性Au-Pd基合金の開発 : Au-Pd合金の磁化率と機械的特性