1117 高強度鋼のODA型き裂進展領域における極低速き裂進展挙動(OS11-4 材料の疲労挙動と損傷評価-超長寿命-)
スポンサーリンク
概要
- 論文の詳細を見る
Fish eye failure that is unique fatigue fracture occurs in very long life region of high strength steel. The fatigue life of Fish eye failure dominated ODA (Optically Dark Area) around the fracture origin. A granular looking area of ODA is visible close to the crack initiation, Fatigue life of Fish eye failure is almost exclusively spent propagating the fatigue clack in ODA. Therefore, to predict fatigue life of Fish-eye failure is important to know ODA of formative mechanism. In this study, fatigue and tensile test was performed in vacuum that simulated environment of subsurface failure and compared the result by the test condition. The observation of Process when ODA is formed on the precrack tip was examined in order to make clear a mechanism of ODA formation. When the tensile stress of 800MPa or less was given, the remarkable growth of the ODA crack was not seen. Crack growth rate has depended on maximum stress by range of ΔK≦4MPam. Under the fixed maximum stress of value, initiated fatigue cracks became non-propagating cracks.
- 一般社団法人日本機械学会の論文
- 2010-10-09
著者
関連論文
- 高強度鋼の高サイクル疲労域における内部き裂進展挙動
- 真空疲労試験による高強度鋼のODA形成条件の検討(疲労)
- 誘導加熱を用いた超急速短時間焼入鋼の引張特性
- 誘導加熱を用いた超急速短時間焼戻鋼の引張特性
- 高濃度浸炭鋼の疲労特性に及ぼす析出炭化物の影響
- フェライト型球状黒鉛鋳鉄の低サイクル疲労特性に及ぼす採取位置の影響
- 高強度鋼の介在物を起点とした疲労き裂進展挙動と破壊モード遷移の関係
- 硬鋼線の張力変動による疲労強度特性(信頼性工学)
- LMCによるCuクラスタリング過程の定量的評価
- Cuクラスタリング過程のLMCシミュレーション