S0402-2-5 粉末冶金プロセスによるTi-Sn-Cr形状記憶合金の作製とその特性([S0402-2]粉末成形とその評価(2))
スポンサーリンク
概要
- 論文の詳細を見る
Ti-Sn-Cr shape memory alloys (SMA) were fabricated by powder metallurgy (PM) process. The mixed powders in composition of Ti-3at%Sn-7at%Cr were prepared using ball milling process. The mixed powders were filled into the graphite die, and then sintered at a temperature of 1023 K and 1223 K using a pulse current sintering method. The sintered alloy was solution-treated and then tempered. The tensile properties and the phase structure of the alloy obtained were investigated. The relative density of the alloy sintered at 1223 K was 99 %. The solution-treated alloy was mainly consisted of the β phase. The alloy tempered at 773 K and 973 K was consisted partly of the a phase. It was found from the result of bending test that the alloy fabricated by the PM process has shape recovery properties.
- 2010-09-04
著者
関連論文
- MIMマルテンサイト系ステンレス鋼の諸特性に及ぼす脱脂条件の影響
- 粉末冶金プロセスと塑性加工による傾斜機能TiNi形状記憶合金ワイヤの作製 : 第1報,TiNi形状記憶合金ビレットの作製とその変態特性
- 1007 傾斜機能TiNi形状記憶合金ワイヤの変態特性(S03-2 形状記憶合金の特性と応用技術(2),21世紀地球環境革命の機械工学:人・マイクロナノ・エネルギー・環境)
- 2105 粉末冶金と塑性加工を組み合わせた傾斜機能TiNi形状記憶合金ワイヤの作製(S06-1 形状記憶合金の特性と応用技術(1),S06 形状記憶合金の特性と応用技術)
- 1910 パルス通電加圧焼結法により作製したTi-Ni形状記憶合金の熱・力学特性に及ぼす合金組成の影響(S17-2 形状記憶合金の特性と応用化技術(2),S17 形状記憶合金の特性と応用化技術)
- パルス通電加圧焼結法によるTi-Ni-Cu合金の形状記憶特性に及ぼす繰返し変形の影響(OS7-1 形状記憶合金の作製とその変形特性,OS7 形状記憶合金の特性と応用化技術)
- 220 パルス通電焼結法により作製した Ti-Ni-Cu 形状記憶合金の熱・力学特性
- 1150 パルス通電加圧焼結法による Ti-Ni/Ti 二層合金の作製
- 845 MA 粉末による Ti-Ni 系合金の形状記憶特性
- 954 放電焼結法により作製した Ti-Ni 形状記憶合金の繰返し特性に及ぼす Cu 添加の影響