G0301-3-4 低温環境下において衝撃負荷を受ける高分子材料に関する研究(材料力学部門一般(3))
スポンサーリンク
概要
- 論文の詳細を見る
High polymer materials are used in various fields, they will be expected to increase use of severe conditions in the future. However, high polymer materials have the feature that the characteristic is easy to change by the use conditions. Therefore, to expand the range of use of high polymer materials further, it is necessary to understand the fracture characteristic by the temperature dependence. In this study, specimens are three kinds of high polymer materials that inserted crack. The crack model assumed V-notch. The experiment temperatures were assumed to be a room temperature, 0, -10, -20, -30, -40 and -50℃. The dynamic stress intensity factor K_1 was determined by using caustics method and impact three-point bending test. As a result, with a fall of the temperature, the maximum value of K_1 showed the tendency to decrease in all materials.
- 社団法人日本機械学会の論文
- 2009-09-12
著者
関連論文
- 107 ポリカーボネートの光劣化とクレーズの発生(機械材料・新素材II)
- 3033 環境薬品の影響によるポリカーボネートおよびクレーズに関する研究(S82-2 サステイナブル・トライボロジー(2),S82 サステイナブル・トライボロジー)
- 209 ポリカーボネートの薬品環境劣化に関する基礎研究(G.S.:材料力学II)
- 206 コースティックス法によるポリカーボネートの低温衝撃に関する研究(材料力学I)
- 4060 ポリカーボネートにおける薬品環境下のクレイズ発生に関する研究(G03-13 き裂進展(2),G03 材料力学)
- P84 ポリカーボネートにおけるクレーズの光劣化の影響(GS11)
- 106 高分子材料におけるクレーズと光劣化に関する基礎研究(機械材料・新素材II)
- 114 ハブベアリングが及ぼす異なる接触状態における自動車用ハブの強度解析(若手優秀講演フェロー賞対象講演(3))
- 20402 光劣化したポリカーボネートにおけるクレーズの挙動(実験力学的手法による生体・材料・製品の評価(1),OS.7 実験力学的手法による生体・材料・製品の評価)
- 16S 光学的手法を用いた変形性膝関節症治療の力学特性に関する研究