光重合型修復材料の寸法変化に影響を及ぼす要因 : 試料保管条件が重合収縮に及ぼす影響
スポンサーリンク
概要
- 論文の詳細を見る
The objective of this study was to examine the effect of specimen storage conditions on the dimensional change of light-cured restorative materials after curing. Ten commercially available conventional composite resins, six different products of flowable type composite resins and three different products of polyacid-modified composite resins were examined. The tapered cylindrical composite resin specimens were prepared using a stainless steel mold and the polymerization shrinkage of specimens after light curing was measured according to the method reported by Bowen et al. The specimens were weighed after determination of curing shrinkage. Then, the specimens were kept for 7 days in either air at 23±2℃ and 50±5% relative humidity or a moisture chamber at 37±2℃ and 95±5% relative humidity. The amounts of dimensional change and the weight of specimens were mensured again after storage of 7 days. In addition, the inorganic filler content in specimens was estimated by burning the specimens at 700℃ in a furnace. All the light-cured restorative materials shrank by light-curing. When the specimens were kept after curing in the moist condition, the amount of contraction was suppressed due to the absorption of water. A positive correlation was found after water sorption between the amounts of changes in weights and in dimensions of specimens. Changes in contraction of specimens after light-curing by water sorption appeared to be related to the nature of the matrix resin in composite resin.
- 特定非営利活動法人日本歯科保存学会の論文
- 2006-06-30
著者
関連論文
- 電気的根管長測定時における複数側枝の影響
- 試作根管充填用水硬性グラスアイオノマーセメントの逆根管充填における根尖部封鎖性について
- 光硬化型コンポマーの逆根管充填における根尖部封鎖性について
- 接着性レジンセメントにおける各種造影材のX線造影性について
- 熱水浸漬がフッ素徐放性修復材料のダイアメトラル引張強さに及ぼす影響
- 熱水浸漬後の支台築造用コンポジットレジンの曲げ強さと圧縮強さの変化
- 光照射後の試料保管条件が可視光線重合型修復材料の重合収縮に及ぼす影響
- 可視光線重合型修復材料の重合収縮について
- 可視光線重合器の光出力が光硬化型修復材の物性に及ぼす影響
- 破断したfileのSEM観察
- フッ素処理フィラーを添加したコンポジットレジンの性質
- 光重合型修復材料の寸法変化に影響を及ぼす要因 : 試料保管条件が重合収縮に及ぼす影響
- 機械的根管形成用器具ライトスピードの根管追従性について