34 溶接残留応力場中のき裂からの脆性破壊発生評価におけるワイブル応力仮説による塑性拘束補正方法

概要

論文の詳細を見る
This paper studies the method for estimating the welding residual stress effect on brittle fracture of structural steel based on the Weibull stress criterion. Using wide plate (WP) specimens with and without welding residual stress, the brittle fracture tests have been conducted at -75℃. The material used is a high strength steel of 780MPa class. Welding residual stress significantly decreases the fracture force and the critical CTOD of the wide plate with welding residual stress at the onset of brittle fracture initiation. And it has been shown that the critical CTOD of the WP specimens can be predicted from fracture test results of the 3-point bend specimens without residual stress based on the Weibull stress criterion. The present paper proposes the assessment method of constraint loss effects on CTOD of wide plate with residual stress based on the equivalent CTOD ratio, βr under residual stress field. The equivalent CTOD ratio, βr is defined as the ratio, δ/δ^r_<WP>, where δ and δ^r_<WP> are CTODs of the standard fracture toughness specimen and wide plate with welding residual stress, respectively, at the same level of the Weibull stress. Fracture assessment results using βr are shown within the framework of failure assessment diagram (FAD). An excessive conservatism observed in the conventional procedure is reasonably reduced by applying the equivalent CTOD ratio, βr.
社団法人日本船舶海洋工学会の論文