437 SiC/AlN複合セラミックスの自己き裂治癒能力の評価(セラミック/セラミック基複合材料)
スポンサーリンク
概要
- 論文の詳細を見る
This study focuses on the crack-healing ability of 50wt.% SiC/50wt.% AlN ceramics obtained by means of pressureless sintering with Y_2O_3 as sintering-aid and without using a powder bed. Semi-elliptical surface cracks from 50μm to 500μm in surface length were introduced at the center of the tensile surface of the specimens. The pre-cracked specimens were heat treated in air for 1h at temperature between 900 and 1300℃ in air. After crack-healing process, monotonic bending tests were carried out. Following experiments were carried out ; (a) Bending strength of pre-cracked specimens with or without crack healing as a function of surface length of pre-cracks, (b) Effects of healing temperature on the bending strength of crack-healed specimens, (c) Effects of test temperature on the bending strength of crack-healed specimens.
- 一般社団法人日本機械学会の論文
- 2006-11-25
著者
関連論文
- K-0904 窒化ケイ素/SiC複合セラミックスのき裂治癒温度(1000℃)での強度特性(G04-1 材料試験・特性評価)(G04 機械材料・材料加工部門一般講演)
- 417 窒化珪素セラミックスの高温酸化挙動(材料工学)
- 1205 成分系が窒化珪素セラミックスの高温酸化挙動に及ぼす影響
- 647 窒化ケイ素/SiC セラミックスの高温疲労特性に及ぼすき裂治癒プロセスの影響
- 637 Mullite/SiC 複合セラミックスき裂治癒材の疲労強度特性
- 1042 キャビテーションピーニングによる人工表面欠陥を有する試験片の疲労限度改善(J12-2 金属材料の疲労特性と破壊機構(2) 表面改質処理,ジョイントセッション,21世紀地球環境革命の機械工学:人・マイクロナノ・エネルギー・環境)
- 1041 キャビテーションピーニングによる軟窒化材の曲げ疲労強度向上(J12-2 金属材料の疲労特性と破壊機構(2) 表面改質処理,ジョイントセッション,21世紀地球環境革命の機械工学:人・マイクロナノ・エネルギー・環境)
- 1302 アルミナ/炭化ケイ素複合材のき裂治癒挙動に及ぼす酸素分圧の影響(J14-1 知的材料・構造システム(1) セラミックスのき裂治癒、強靭化,ジョイントセッション,21世紀地球環境革命の機械工学:人・マイクロナノ・エネルギー・環境)
- 引張残留応力場から圧縮残留応力場にき裂が伝播する場合の溶接残留応力の再配分とき裂進展挙動(OS6-3 損傷評価・計測,OS6 エネルギー機器の維持管理と健全性評価)
- 649 炭化珪素セラミックスき裂治癒挙動と治癒材の高温強度特性
- 1204 オーステナイト系ステンレス鋼 SUS304 の鋭敏化の検出
- 表面き裂材の疲労寿命とき裂貫通挙動 : 第1報,引張荷重を受ける場合
- 1251 局部減肉がティ配管の低サイクル疲労破損挙動に及ぼす影響(G03-8 材料力学(8)疲労・強度1,21世紀地球環境革命の機械工学:人・マイクロナノ・エネルギー・環境)
- 613 応力二段ショットピーニングに関する研究
- 2537 き裂治癒によるセラミックスの耐熱衝撃性の向上(J10-8 き裂治癒,J10 知的材料・構造システム)
- 437 SiC/AlN複合セラミックスの自己き裂治癒能力の評価(セラミック/セラミック基複合材料)