3620 キャビテーション・ピーニングによる軽金属材料の疲労強度向上(G03-3 表面改質,G03 材料力学)
スポンサーリンク
概要
- 論文の詳細を見る
Cavitation normally causes severe damage in hydraulic machinery such as pumps and valves so on. However, cavitation impact can be utilized to surface treatment to improve fatigue strength of metallic materials in the same way as shot peening. Peening using cavitation impact was named as "cavitation peening" or "cavitation shotless peening" as shots are not required. As increase of surface roughness induced by cavitation peening was relatively small comparing with that of shot peening, improvement of fatigue strength of light metallic materials would be better than that of shot peening. In the present paper, the aluminum alloy and the magnesium alloy treated by cavitation peening were tested by a rotating bending fatigue test. It was revealed that the fatigue strength of the aluminum alloy AC4CH and magnesium alloy AM60B were improved 40% and 20%, respectively.
- 2006-09-15
著者
関連論文
- Jet Structure Analyses on High-Speed Submerged Water Jets through Cavitation Noises
- Several Kinds Vibrations Arisen around a Typical Highspeed SupercavitatingHydrofoil with Various Nose Shapes
- Singular Behavior of Erosion-Standoff-Distance-Curves for Highspeed-Water-Jets in Air
- Behavior of Cavitation Nuclei in High-Speed Submerged Water-Jet-Tests
- 211 大気中アーク放電による炭素鋼表面の硬度向上(材料評価II)
- 遠心ポンプに発生する高壊食性渦キャビテーションの観察
- ピーニングされた表面の摩擦・摩耗特性(S45C焼入れ材の場合)
- 220 キャビテーション気泡の崩壊衝撃力によるカバレージの経時変化の数値シミュレーション
- キャビテーション損傷の潜伏期の定量的予測に関する一考察
- 908 キャビテーションピーニングを施した鋼ローラの表面性状とピッチング強さ(模索潤滑設計II)