Microwave Dielectric Properties and Microstructures of Ca_<1-x>Nd_<2x/3>TiO_3-Li_<1/2>Nd_<1/2>TiO_3 Ceramics
スポンサーリンク
概要
- 論文の詳細を見る
The microwave dielectric properties and microstructures of (1 - y) Ca_<1-x>Nd_<2x/3>TiO_3-Li_<1/2>Nd_<1/2>TiO_ ceramics, prepared by a mixed oxide route, have been investigated. A maximum quality factor Q x f = 8600 GHz (where f is the resonant frequency) was achieved for samples with y = 0 and x = 0.39, although the dielectric properties varied with sintering temperature. The Q x f value of (1 - y) Ca_<1-x>Nd_<2x/3>TiO_3-Li_<1/2>Nd_<1/2>TiO_3 increased up to 1400℃, after which it decreased. The decrease in dielectric properties was coincident with the onset of rapid grain growth. In the (1 - y)Ca_<1-x>Nd_<2x/3>TiO_3-Li_<1/2>Nd_<1/2>TiO_3-y Li_<1/2>Nd_<1/2>TiO_3 system, as y increased, the temperature coefficient of resonant frequency Cry) decreased from 800 to 8 ppm/℃ for y = 0.52 (x = 0.39). However, the optimum combination of microwave dielectric properties was achieved at 1400℃ for samples where y = 0.45 (x = 0.39) with a dielectric constant Sr of 101, a Q x f value of 5300 (at 7.2 GHz) and a τ_f value of + 13 ppm/℃.
- 社団法人応用物理学会の論文
- 2002-09-15
著者
-
Chen Hui-liang
Tainan Woman's College Of Art And Technology
-
Huang Cheng-liang
Department Of Electrical Enggineering National Cheng-kung University
関連論文
- New Dielectric Material System of La(Mg_Ti_)O_3-CaTiO_3 at Microwave Frequencies
- Liquid Phase Sintering and Microwave Dielectric Properties of NdAlO_3 Ceramics
- Effect of B_2O_3 Additives on Sintering and Microwave Dielectric Behaviors of CuO-Doped ZnNb_2O_6 Ceramics
- Analysis and Simulation of Stacked-Segment Electromechanical Transducers with Partial Electrical Excitation by PSPICE
- Computer Simulation of Direct-Current Field Dependence of the Dielectric Constant of Al_2O_3-Doped Barium Stronium Titanate in the Paraelectric State
- SAW Sensors of Organophosphorous Compound with No Humidity Interference
- The Microwave Dielectric Properties and the Microstructures of Bi(Nb, Ta)O_4 Ceramics
- Improved High-Q Dielectric Resonator Sintered at Low Firing Temperature
- Dielectric Properties of CaTiO_3-Ca(Mg_Nb_)O_3 Ceramic System at Microwave Frequency
- The Microwave Dielectric Properties and the Microstructures of La_2O_3-Modified BiNbO_4 Ceramics